Abstract:NO catalytic oxidation (NOCO) to NO2 is widely believed to be a fundamental step in selective catalytic reduction (SCR) over activated carbon (AC). Thus, the enhancement of NOCO over AC is significant. The effect of the pore structure on NOCO is discussed first. A series of microporous AC samples with various microporous surface areas were prepared, in which a strong positive correlation existed between NO conversion and the microporous surface area. With an increase in the microporous surface area, the NO conversion increased from 13.10% for MAC1 to 41.18% for MAC4. Concurrently, a hierarchical AC sample with an approximate hierarchy degree (the ratio of V mes+mac to V t ) of 50% demonstrated higher NO conversion than microporous AC when the microporous surface areas were similar. HAC2 exhibited the largest NO conversion (51.58%). Therefore, the microporous surface area and degree of hierarchy are key factors that enhance NO conversion. NOCO has been demonstrated to be an O-enriched process. In situ diffuse reflectance infrared Fourier transform spectroscopy (DRIFT) results revealed that carbonyl groups were generated during the NOCO process. Density functional theory calculations were then performed. Carbonaceous models with unsaturated C atom, carbonyl, and lactone groups were constructed, and the corresponding NOCO reaction paths were calculated. A dual-site NOCO mechanism was proposed by combining the experimental and calculation results. Two types of active sites existed: unsaturated C atoms and high-spin density C atoms that affected the kinetic and steady-state stages of NOCO, respectively. The total amount of high-spin density C atoms strongly depends on the microporous surface area. The study of NOCO was updated, which contributed to the preparation of highly efficient AC for NOCO.

The Role of Surface Properties of Activated Carbon in the Catalytic Reduction of NO by Carbon

Effect of Pretreatment Method of Activated Carbon on the Catalytic Reduction of NO by Carbon over CuO

Effect of Nitric Acid Pretreatment on the Properties of Activated Carbon and Supported Palladium Catalysts

Effect of Nitrogen Doping on the Reduction of Nitric Oxide with Activated Carbon in the Presence of Oxygen

Catalytic reduction of NO on the catalysts supported on activated carbon fibers. I. Copper-series catalysts

Selective catalytic reduction of NO with NH3 over CuOX-carbonaceous materials

Catalytic reduction of NO on the catalysts supported on activated carbon fibers. II. Nickel-series catalysts

Activation of Fast Selective Catalytic Reduction of NO by NH3 at Low Temperature over TiO2 Modified CuOX-CeOX Composites

Highly active and stable Cu Fe /AC-H catalysts with CuFe2O4 for NO reduction by CO in the presence of H2O and SO2 under regeneration gas

SURFACE MODIFICATION AND ADSORPTION PROPERTY OF ACTIVATED CARBON BY HNO_3

The effect of the oxidation method of an activated carbon on the selective catalytic reduction of NOx with NH3 over CeO2/activated carbon catalysts

Effect of Activated Carbon and Its Surface Property on the Activity of Ru/Ac Catalyst

Influence of the Surface Oxygenated Groups of Activated Carbon on Preparation of A Nano Cu/Ac Catalyst and Heterogeneous Catalysis in the Oxidative Carbonylation of Methanol

Simultaneous removal of NO x and SO 2 by low-temperature selective catalytic reduction over modified activated carbon catalysts

Insight into the promotion mechanism of activated carbon on the monolithic honeycomb red mud catalyst for selective catalytic reduction of NOx

An updated study on NO catalytic oxidation over activated carbon: The effect of pore structure and a dual-site mechanism

Surface Tailoring on Bifunctional CuOx/MnO2 Catalyst to Promote the Selective Catalytic Reduction of NO with NH3 and Oxidation of CO with O2

Promoting Role of Potassium on the Catalytic Performance of Copper Oxide for the Reduction of NO by Activated Carbon

Effect of Original Activated Carbon Support and the Presence of NOx on CO Oxidation over Supported Wacker-type Catalysts

Catalytic Oxidation of NO on Activated Carbons

Surface Modification of Activated Coke for NO Oxidation at Ambient Temperature