Abstract:In this work, Ce and Mn were added to Cu-SSZ-39 zeolites by ion-exchange process, and their activity performance for selective catalytic reduction of NOx with ammonia (NH3-SCR), especially hydrothermal stability (hydrothermal aging at 750, 800, 850 °C) was investigated systematically. It is found that the addition of Ce and Mn, Mn more evidently, both can greatly improve the activity of Cu-SSZ-39 catalyst. Moreover, MnCu-SSZ-39 catalyst have shown superior hydrothermal stability compared with Cu-SSZ-39 catalyst, and outstandingly its activity is not only not decreased significantly like Cu-SSZ-39 but improved obviously after hydrothermal aging at as high as 850°C. The high and improved activity of Ce and Mn added Cu-SSZ-39 is ascribed to more active CuO crystallites formation in the inner channel and higher acidity strength. The superior hydrothermal stability of MnCu-SSZ-39 may be due to its well-preserved structure and acid density even after hydrothermal aging at as high as 850 °C. Moreover, during the hydrothermal aging process, not only Cu oxides aggregation is inhibited, but also more Cu2+ ion species are induced to ion exchange sites in MnCu-SSZ-39, which may account for its excellent hydrothermal stability (even higher than the activity of fresh samples). The mechanism analysis has shown NH3-SCR reaction over Cu-SSZ-39 and CeCu-SSZ-39 samples follow the "Langmuir−Hinshelwood" (L-H) mechanism, while on MnCu-SSZ-39, it follows both "L−H" and "Eley−Rideal" (E−R) mechanisms, which may also be another reason for its excellent activity and hydrothermal stability. Moreover, "Fast SCR" mechanisms also occur and contribute over hydrothermal aged A-MnCu-SSZ-39 sample, in addition to "L-H" and "E-R" mechanisms. Thus, the easily prepared MnCu-SSZ-39 catalyst has shown the excellent activity and super hydrothermal stability, with 90% NO conversion at 245 °C and broader temperature window of 245 °C to 550 °C, even after hydrothermal aging at 850 °C, therefore indicate great potential for future application in NOx purifying from diesel engine exhaust.

Insight into the promotion mechanism of activated carbon on the monolithic honeycomb red mud catalyst for selective catalytic reduction of NOx

In Situ DRIFTS Studies of NH3-SCR Mechanism over V2O5-CeO2/TiO2-ZrO2 Catalysts for Selective Catalytic Reduction of NOx

The Promotion of NH3-SCR Performance by AC Addition on Mn-Fe/Z Catalyst

Low-temperature SCR of NO with NH3 over AC/C Supported Manganese-Based Monolithic Catalysts

Iron Doped Effects on Active Sites Formation over Activated Carbon Supported Mn-Ce Oxide Catalysts for Low-Temperature SCR of NO

Acid-pretreated red mud for selective catalytic reduction of NO with NH3: Insights into inhibition mechanism of binders

Promotional Mechanism of La-Mn-Fe Modification on Activated Coke for NH3-SCR of NOx at Low Temperatures

The Utilization of Red Mud Waste As Industrial Honeycomb Catalyst for Selective Catalytic Reduction of NO

Precise regulation of acid pretreatment for red mud SCR catalyst: Targeting on optimizing the acidity and reducibility

Selective catalytic reduction of NOx with NH3 by monolithic catalyst MnOx/AC/C under low temperature in the presence of excess O2

Application of a New Carbonaceous Catalyst in NH3 Selective Catalytic Reduction(scr) of NOx

Promotion effect of nitrogen doping on the low-temperature NH 3 -SCR of NO over activated carbon: Characterization and mechanism analysis

Spinel Structured CoaMnbOx Mixed Oxide Catalyst for the Selective Catalytic Reduction of NOx with NH3

Promotional effect of rare earth-doped manganese oxides supported on activated semi-coke for selective catalytic reduction of NO with NH3

Modified red mud catalyst for the selective catalytic reduction of nitrogen oxides: Impact mechanism of cerium precursors on surface physicochemical properties

Synergistic Promotion Effect of Acidity and Redox Capacity in the Simultaneous Removal of CB and NOx in NH3-SCR Unit

Selective Catalytic Reduction Of Nox With Nh3 At Low Temperatures Over Metal Oxide Supported On Ac-C Cellular Monoliths

The Role of Surface Properties of Activated Carbon in the Catalytic Reduction of NO by Carbon

CrO3 Supported on Sargassum-Based Activated Carbon As Low Temperature Catalysts for the Selective Catalytic Reduction of NO with NH3

Advances in Selective Catalytic Reduction of NO with Methane

Promoting effect of Ce and Mn addition on Cu-SSZ-39 zeolites for NH3-SCR reaction: Activity, hydrothermal stability, and mechanism study