Abstract:We first present preparation of MnOx–CeO2–Al2O3 catalysts with varying Mn contents through a self-propagating high-temperature synthesis (SHS) method, and studied the application of these catalysts to the selective catalytic reduction of NOx with NH3 (NH3-SCR). Using the catalyst with 18 wt.% Mn (18MnCe1Al2), 100% NO conversion was achieved at 200°C and a gas hourly space velocity of 15384hr−1, and the high-efficiency SCR temperature window, where NO conversion is greater than 90%, was widened to a temperature range of 150–300°C. 18MnCe1Al2 showed great resistance to SO2 (100 ppm) and H2O (5%) at 200°C. The catalysts were characterized using X-ray diffraction, X-ray photoelectron spectroscopy, Brunauer–Emmett–Teller (BET) analysis, scanning electron microscopy, Fourier transform infrared spectroscopy, and H2 temperature programmed reduction. The characterization results showed that the surface atomic concentration of Mn increased with increasing Mn content, which led to synergism between Mn and Ce and improved the activity in the SCR reaction. 18MnCe1Al2 has an extensive pore structure, with a BET surface area of approximately 135.4m2/g, a pore volume of approximately 0.16cm3/g, and an average pore diameter of approximately 4.6 nm. The SCR reaction on 18MnCe1Al2 mainly followed the Eley-Rideal mechanism. The performances of the MnOx–CeO2–Al2O3 catalysts were good, and because of the simplicity of the preparation process, the SHS method is applicable to their industrial-scale manufacture.

Mnox/Ceo2/Sio2 Catalysts Prepared by Adsorption Phase Reaction Technique for Selective Catalytic Reduction of Nox at Low-Temperature

Influence of Mn/(Mn+Ce) Ratio of MnOx-CeO2/WO3-ZrO2 Monolith Catalyst on Selective Catalytic Reduction of NOx with Ammonia

Novel Homogeneous and Mesoporous MnOx-Doped Ceria Nanosheets As Catalysts for Low-Temperature Selective Catalytic Reduction

CeO2 Nanoparticle-Loaded MnO2 Nanoflowers for Selective Catalytic Reduction of NOx with NH3 at Low Temperatures

Highly Selective Catalytic Reduction of NOx by MnOx–CeO2–Al2O3 Catalysts Prepared by Self-Propagating High-Temperature Synthesis

The activity and characterization of MnOx–CeO2–ZrO2/γ-Al2O3 catalysts for low temperature selective catalytic reduction of NO with NH3

Preparation of Cr-Mn Mixed Oxide by Coprecipitation and Its Performance for Low-Temperature Selective Catalytic Reduction of NOx

Mn0·4/Co0·1Ce 0·45Zr0·45OX, high performance catalyst for selective catalytic reduction of NO by ammonia

Catalytic performance of CeO2-NPs and α-MnO2 mixed oxides catalysts for low-temperature NH3-SCR of NO

Selective catalytic reduction of NO with NH3 over MnOx-CeO2 catalysts: The great synergy between CeO2 and crystalline phase of Mn3O4

Effect of Ceria Doping on Catalytic Activity and SO2 Resistance of MnOx /tio2 Catalysts for Selective Catalytic Reduction of NO with NH3 at Low Temperature

Unraveling the synergy between MnOx and CeO2 in MnOx-CeO2 SCR catalysts based on experimental and DFT studies

Selective Catalytic Reduction of NOx with NH3 over Mn-Ce Mixed Oxide Catalyst at Low Temperatures

Synthesis of Both Powdered and Preformed MnOx–CeO2–Al2O3 Catalysts by Self-Propagating High-Temperature Synthesis for the Selective Catalytic Reduction of NOx with NH3

In Situ Supported Mnox-Ceox On Carbon Nanotubes For The Low-Temperature Selective Catalytic Reduction Of No With Nh3

Transition Metal Doped MnOx-CeO2 Catalysts by Ultrasonic Immersing for Selective Catalytic Reduction of NO with NH3 at Low Temperature

Low-temperature Selective Catalytic Reduction of NO with NH3 over Monolith Catalyst of MnOx/CeO2–ZrO2–Al2O3

Molybdenum-containing oxide catalysts for selective catalytic reduction of NOx with NH3

Novel Mn-Ce-Ti Mixed-Oxide Catalyst for the Selective Catalytic Reduction of NOx with NH₃.

Low-temperature selective catalytic reduction of NO with NH3 over Mn–Ce–Ox/TiO2: a comparison between catalyst preparation methods

Low-temperature SCR of NO with NH3 over AC/C Supported Manganese-Based Monolithic Catalysts