Abstract:ZnO based diluted magnetic semiconductor particles (ZnO:Co) have been grown using a hydrothermal method with good crystallinity. The atomic percentage of Co presented in the specimen is about 0.01. Based on the x-ray diffraction and high-resolution transition electron, Co is found to be incorporated into ZnO lattice without evidence of obvious Co precipitates. However, from photoluminescence (PL) spectra in the range of 1.94 –3.45eV, a strong broad emission centered around 600nm (2.07eV) in the visible range as well as a relatively weak peak at 2.81eV are observed, indicating the presence of Co impurities. Moreover, intrinsic emissions such as DOX suggest that at least some Co have been doped into ZnO lattice, substituting for Zn2+ ions. The PL results further confirm the substitution of Zn2+ ions by Co, which leads to the changes of the electronic band structures. Magnetism could be realized at room temperature for the ZnO:Co nanoparticles under our experimental conditions although with low coercivity. The field-cooled and zero-field-cooled curves can be explained as a result of competition between the ferromagnetic and the antiferromagnetic ordering in the ZnO:Co nanoparticles. Combining the results from PL and magnetism characterization, it is reasonable to think that both doped Co in the ZnO lattice and Co impurities contribute to magnetism in ZnO:Co nanoparticles at room temperature.

Room Temperature Magnetism in Sputtered Co/sub X/zn/sub 1-X/o Films

Room Temperature Magnetism in Sputtered (zn,co)o Films

Characterization of ZnO:Co particles prepared by hydrothermal method for room temperature magnetism

Room-temperature Ferromagnetism in Co-doped ZnO Diluted Magnetic Semiconductor

Room temperature magneto-optics of ferromagnetic transition-metal doped ZnO thin films

Room-Temperature Fabricated Zncoo Diluted Magnetic Semiconductors

Origin Of Room Temperature Ferromagnetism In Mgo Films

The Magnetic Properties of Co-Doped Zno Diluted Magnetic Insulator Films Prepared by Direct Current Reactive Magnetron Co-Sputtering

Growth Temperature Dependent Evolutions of Microstructural, Optical and Magnetic Properties of Zn0.75Co0.25O Films

Room-temperature Ferromagnetism in Mn-doped SnO2 Diluted Magnetic Semiconductor

Room-Temperature Ferromagnetism in P-Type (mn, N)-Codoped Zno Thin Films Achieved by Thermal Oxidation of Sputtered Zn3n2 : Mn Films

Room Temperature Multiferroicity in Zn 0.98 Cu 0.02 O Film Prepared in N Plasma

Room-Temperature Ferromagnetic Znmno Thin Films Synthesized by Plasma Enhanced Chemical Vapour Deposition Method

High Temperature Ferromagnetism with Giant Magnetic Moment in Transparent Co-doped SnO2-d

Room temperature ferromagnetism in transparent and conducting Mn-doped $SnO_{2}$ thin films

Room Temperature Ferromagnetic Pure Zno

Room-Temperature Magnetism in Cr-Doped Aln Semiconductor Films

Room temperature ferromagnetic and ultraviolet optical properties of Co-doped ZnO nanocluster films

Transition from Diluted Magnetic Insulator to Semiconductor in Co-Doped Zno Transparent Oxide

Confirmation of Room Temperature Ferromagnetism for Mn-doped ZnO Micro-Tetrapod Powders

Magnetic and Transport Properties of (mn, Co)-Codoped Zno Films Prepared by Radio-Frequency Magnetron Cosputtering