Abstract:Ferromagnetic metallic oxides have potential applications in spincaloric devices which utilize the spin property of charge carriers for interconversion of heat and electricity through the spin Seebeck or the anomalous Nernst effect or both. In this work, we synthesized polycrystalline La0.5S0.5CoO3 by microwave irradiation method and studied its transverse thermoelectric voltage (Nernst thermopower) and change in the linear dimension of the sample (Joule magnetostriction) in response to external magnetic fields. In addition, magnetization, temperature dependences of electrical resistivity, and longitudinal Seebeck coefficient (Sxx) in absence of an external magnetic field were also measured. The sample is ferromagnetic with a Curie temperature of TC = 247 K and shows a metal-like resistivity above and below TC with a negative sign of Sxx suggesting charge transport due to electrons. Magnetic field dependence of the Nernst thermopower (Sxy) at a fixed temperature shows a rapid increase at low fields and a tendency to saturate at high fields as like the magnetization. Anomalous contribution to Sxy was extracted from total Sxy measured and it exhibits a maximum value of ~ 0.21 microV/K at 180 K for H = 50 kOe, which is comparable to the value found in a single crystal for a lower Sr content. The Joule magnetostriction is positive, i.e., the length of the sample expands along the direction of the magnetic field and it does not saturate even at 50 kOe. The magnetostriction increases with decreasing temperature below TC and reaches a maximum value of 500 ppm at T = 40 K and below. Coexistence of the anomalous Nernst thermopower and giant magnetostriction in a single compound has potential applications for thermal energy harvesting and low-temperature actuators, respectively.

High Temperature Ferromagnetism with Giant Magnetic Moment in Transparent Co-doped SnO2-d

Giant Magnetic Moment In An Anomalous Ferromagnetic Insulator: Co-Doped Zno

Room temperature ferromagnetism in transparent and conducting Mn-doped $SnO_{2}$ thin films

High-performance Colossal Permittivity Behaviour Persists to Ultralow Temperature in Co+Ta Co-Doped SnO2: A Spin-Defect Mediated Superstable Large Electronic Moment of Defect-Dipole

Co-Doped La0.5sr0.5tio3-Delta: Diluted Magnetic Oxide System With High Curie Temperature

Co-doped La1-xSrxTiO3 : A Diluted Magnetic Metal with High Curie Temperature

Giant Positive Magnetoresistance in Co@CoO Nanoparticle Arrays

Room Temperature Magnetism in Sputtered Co/sub X/zn/sub 1-X/o Films

The Magnetic Properties of Co-Doped Zno Diluted Magnetic Insulator Films Prepared by Direct Current Reactive Magnetron Co-Sputtering

Is room temperature ferromagnetism possible in K-doped SnO2?

Room-temperature Ferromagnetism in Mn-doped SnO2 Diluted Magnetic Semiconductor

ROOM TEMPERATURE FERROMAGNETISM IN (N, Co)-CODOPED ZnO THIN FILMS

Ferromagnetism at 300 K in spin-coated films of Co doped anatase and rutile TiO2

Emergent high-temperature insulating ferromagnetism in Sr4Fe5CoO13- δ epitaxial thin films

Room-temperature ferromagnetism in transparent Mn-doped BaSnO3 epitaxial films

Complex room temperature ferrimagnetism induced by zigzag oxygen-vacancy stripes in Sr3YCo4O10.72

Electronic Structure Using Powder XRD and Its Correlation with the Origin of Room-Temperature Magnetism in Cr3+ Doped SnO2

Anomalous Nernst thermopower and giant magnetostriction in microwave synthesized La0.5Sr0.5CoO3

Room Temperature Ferromagnetic Semiconductor Rutile Ti1-xCoxO2-δEpitaxial Thin Films Grown by Sputtering Method

Intrinsic room temperature ferromagnetism in Co-implanted ZnO

Giant Room-Temperature Magnetocapacitance In Co2+ Doped Sno2 Dielectric Films