Abstract:The non-uniform corrosion of steel bars is the main factor affecting the durability of concrete. The cracking pattern of concrete due to corrosion is closely related to the distribution of the corrosion products. Research on the thickness distribution of the rust layer and the cracking pattern of concrete under different influencing factors is of great significance in the prediction of the service life of existing reinforced concrete structures and the avoidance of the premature cracking of the reinforced concrete structures to be built. This paper studies the thickness distribution of the rust layer on the surface of single and multiple corroded reinforcements under non-uniform corrosion. The electrochemical analysis of the electrified corrosion process was carried out by using the finite element analysis software, and the distribution of the current density was obtained. The effects of geometric parameters, steel bar position, and steel bar spacing and shape on the corrosion expansion cracking pattern were studied. The results indicated that as the position of the steel bar differed, the crack pattern of the concrete changed, depending on the number of corrosion peaks (i.e., the maximum thickness of the rust layer). In terms of the corner-located steel, the number of corrosion peaks varied in the cases of different geometrical parameters (i.e., the diameter of the steel bar and the distance between the steel bars and the stainless steel wire). Nevertheless, the critical corrosion degrees of the side-located and corner-located steel bars, with respect to the cracking of the outer concrete surface, were basically the same. Additionally, the ribbed steel bar presented a lower critical corrosion degree than that of the plain steel bar, while little influence was exhibited with the varying angles of the rib.

Non-uniform distribution of rust layer around steel bar in concrete

Non-Uniform Distribution of A Corrosion Layer at A Steel/Concrete Interface Described by A Gaussian Model

Rust Distribution And Corrosion-Induced Cracking Patterns Of Corner Located Rebar In Concrete Cover

Applicability Discussion for Multi-Peak Gaussian Model of Corrosion Layer at Steel/concrete Interfaces

Critical thickness of rust layer at inner and out surface cracking of concrete cover in reinforced concrete structures

Crack shape and rust distribution in corrosion-induced cracking concrete

Distribution of millscale on corroded steel bars and penetration of steel corrosion products in concrete

Comparison of Uniform and Non-Uniform Corrosion Induced Damage in Reinforced Concrete Based on a Gaussian Description of the Corrosion Layer

Rust Distribution of Non-Uniform Steel Corrosion Induced by Impressed Current Method

Mill Scale and Corrosion Layer at Concrete Surface Cracking

Study on Experimental Method and Morphology of Accelerated Non-Uniform Corrosion of Steel Bars

Study On Distribution Of Steel Corrosion Products In Concrete Structures

Study On Modulus Of Rust Applied In Steel Corrosion Induced Concrete Cracking Model

A Self-Balanced Electrochemical Model for Corrosion of Reinforcing Steel Bar in Considering the Micro-Environments in Concrete

Non-uniform model of relationship between surface strain and rust expansion force of reinforced concrete

Modelling the corrosion mechanism of steel bars in chloride-contaminated concrete with transverse cracks

Behavior Of Rust Expansion Cracking Of Concrete Deduced By Equivalent Corrosion Products Of Steel Bar

Cover Cracking Model in Reinforced Concrete Structures Subject to Rebar Corrosion

Crack shape and rust distribution in corrosion-induced cracking concrete coupled with load

Fractal Characterization of Non-Uniform Corrosion of Steel Bars in Concrete Beams after Accelerated Depassivation and Seven-Year Natural Corrosion.

Non-uniform Corrosion of Steel in Mortar Induced by Impressed Current Method: an Experimental and Numerical Investigation