Abstract:In this work, the non-uniform corrosion characteristics of steel bars in stressed reinforced concrete beams after accelerated depassivation and seven-year outdoor natural corrosion is analyzed using fractal theory. 3D laser scanning and 3D reconstruction technology are applied to collect the cross-sectional area along the steel bars and obtain the corrosion curves. The non-uniformity of corrosion is analyzed by fractal dimensions which is calculated by variation method. The results indicate that the initial loading level and loading zone have some influence on non-uniform characteristics of steel bars. For an ordinary concrete beam, the increase of load can cause a reduction of fractal dimension of corrosion curves by 5%, which indicates the non-uniformity of corrosion will increase with the increase of load level. The fractal dimension in the bending zone is lower than that in the tension-shear zone, which indicates that corrosion is more non-uniform in bending zone. However, the loading level and loading zone have a slight influence on corrosion level, and the maximum difference of corrosion level caused by load is merely 0.23%. Furthermore, the corrosion level increases with the decrease of fractal dimension, suggesting that the non-uniformity of corrosion increases with the growth of corrosion level. The incorporation of slag powder can help reduce the non-uniformity of corrosion, but the influence on reduction of the corrosion level is about 0.25%. For concrete structures under marine environment, application of slag powder is a good method to slow down the corrosion and reduce the non-uniformity of corrosion.

Comparison of Uniform and Non-Uniform Corrosion Induced Damage in Reinforced Concrete Based on a Gaussian Description of the Corrosion Layer

Non-Uniform Distribution of A Corrosion Layer at A Steel/Concrete Interface Described by A Gaussian Model

Applicability Discussion for Multi-Peak Gaussian Model of Corrosion Layer at Steel/concrete Interfaces

Non-uniform distribution of rust layer around steel bar in concrete

State-of-art of corrosion-induced cracking of reinforced concrete structures

Stochastic Characteristics of Reinforcement Corrosion in Concrete Beams under Sustained Loads

Analytical Model for Non-Uniform Corrosion-Induced Concrete Cracking

Experimental Investigation of Corrosion-Induced Cover Cracking in Reinforced Concrete Structures

Study on Experimental Method and Morphology of Accelerated Non-Uniform Corrosion of Steel Bars

Fractal Characterization of Non-Uniform Corrosion of Steel Bars in Concrete Beams after Accelerated Depassivation and Seven-Year Natural Corrosion.

Data-driven Corrosion Failure Probabilistic Assessment Model for Reinforced Concrete Structures

Experimental Study on Distribution of Corrosion Products in Corrosion-Induced Cracks in Reinforced Structures

Non-Uniform Corrosion-Induced Reinforced Concrete Cracking: an Analytical Approach

Numerical Modeling of Nonuniform Corrosion-Induced Concrete Crack Width

Fractal Characteristics of Corrosion-Induced Cracks in Reinforced Concrete.

Damage Analysis and Cracking Model of Reinforced Concrete Structures with Rebar Corrosion

Simulation and Experimental Verification of the Non-Uniform Corrosion Cracking Process of Reinforced Mortar Specimen

Corrosion-induced concrete cracking model considering corrosion product-filled paste at the concrete/steel interface

On the Penetration of Corrosion Products from Reinforcing Steel into Concrete Due to Chloride-Induced Corrosion

Rust Distribution And Corrosion-Induced Cracking Patterns Of Corner Located Rebar In Concrete Cover

Crack shape and rust distribution in corrosion-induced cracking concrete