Abstract:In this work, the non-uniform corrosion characteristics of steel bars in stressed reinforced concrete beams after accelerated depassivation and seven-year outdoor natural corrosion is analyzed using fractal theory. 3D laser scanning and 3D reconstruction technology are applied to collect the cross-sectional area along the steel bars and obtain the corrosion curves. The non-uniformity of corrosion is analyzed by fractal dimensions which is calculated by variation method. The results indicate that the initial loading level and loading zone have some influence on non-uniform characteristics of steel bars. For an ordinary concrete beam, the increase of load can cause a reduction of fractal dimension of corrosion curves by 5%, which indicates the non-uniformity of corrosion will increase with the increase of load level. The fractal dimension in the bending zone is lower than that in the tension-shear zone, which indicates that corrosion is more non-uniform in bending zone. However, the loading level and loading zone have a slight influence on corrosion level, and the maximum difference of corrosion level caused by load is merely 0.23%. Furthermore, the corrosion level increases with the decrease of fractal dimension, suggesting that the non-uniformity of corrosion increases with the growth of corrosion level. The incorporation of slag powder can help reduce the non-uniformity of corrosion, but the influence on reduction of the corrosion level is about 0.25%. For concrete structures under marine environment, application of slag powder is a good method to slow down the corrosion and reduce the non-uniformity of corrosion.

Stochastic Characteristics of Reinforcement Corrosion in Concrete Beams under Sustained Loads

Probability-Based Performance Degradation Model and Constitutive Model for the Buckling Behavior of Corroded Steel Bars

Crack shape and rust distribution in corrosion-induced cracking concrete coupled with load

Corrosion-induced Shear Performance Degradation of Reinforced Concrete Beams

Corrosion-Induced Cracking Propagation Of Rc Beams Subjected To Different Corrosion Methods And Load Levels

Prediction of Corrosion-Induced Concrete Cracking under External Loading and Stirrup Constraint

Time-dependent reliability analysis of reinforced concrete beams subjected to bending and marine atmospheric environment

Fractal Characterization of Non-Uniform Corrosion of Steel Bars in Concrete Beams after Accelerated Depassivation and Seven-Year Natural Corrosion.

Crack Propagation and Flexural Behaviour of Rc Beams under Simultaneous Sustained Loading and Steel Corrosion

Corrosion Characteristics of A 4-Year Naturally Corroded Reinforced Concrete Beam with Load-Induced Transverse Cracks

Effects of Reinforcement Corrosion and Sustained Load on Mechanical Behavior of Reinforced Concrete Columns.

Study On Distribution Of Steel Corrosion Products In Concrete Structures

Corrosion-crack path based probabilistic model to predict the durability behavior of RC components

Corrosion Damages of Reinforced Concrete Characterized by X-ray CT and DVC Techniques

Prediction of Corrosion-Induced Crack Width of Corroded Reinforced Concrete Structures

Performance of Reinforced Concrete Beams Corroded under Sustained Service Loads: A Comparative Study of Two Accelerated Corrosion Techniques

Effect of Corrosion on Bond Behavior and Bending Strength of Reinforced Concrete Beams

Study on Experimental Method and Morphology of Accelerated Non-Uniform Corrosion of Steel Bars

Shear Performance of Reinforced Concrete Beams with Corroded Stirrups in Chloride Environment

The Corrosion Characteristics And Tensile Behavior Of Reinforcement Under Coupled Carbonation And Static Loading

Monotonic and fatigue behavior of steel-concrete composite beams subjected to corrosion