Mill Scale and Corrosion Layer at Concrete Surface Cracking

Yuxi Zhao,Weiliang Jin

DOI: https://doi.org/10.1016/b978-0-12-809197-5.00005-0

2016-01-01

Abstract:Electrochemically corroded reinforced concrete specimens are observed by a digital microscope and a scanning electron microscope to study the critical thickness of the corrosion layer at concrete inner and outer surface cracking; the rust distributed at the steel–concrete interface and in corrosion-induced cracks are also investigated. This study found that a uniform mill scale layer exists on the surface of the corroded steel bar and that rust does not fill the corrosion-induced cracks before concrete surface cracking in the electrochemically corroded reinforced concrete specimens.