Abstract:Time-to-cracking of the concrete cover induced by the steel corrosion is one of the critical problems faced by engineers, operators and asset managers in making strategies for the maintenance and repairs of reinforced concrete (RC) structures affected by corrosion. In this paper, a theoretical model for predicting the time-to-cracking is derived by assuming the bond between the steel bar and the concrete as a linear combination of perfectly smooth and bonded. The model takes into account the characteristics of existing exiguous flaws and initial cracks in the concrete before the load acting on RC structures. The validity of the proposed model is preliminarily verified by comparing the obtained results with the available experimental results. A remarkable advantage of the proposed method is its application to the prediction of the service life of RC structures, made of the deformed steel bars as well as the round bars. By determining an experimental constant α , which is related to the interface bond state between the steel bar and the concrete, the service life of RC structures can be predicted using the proposed scheme. Analysis of major factors affecting the time-to-cracking demonstrates that the length of the initial crack affects the service life of RC structures significantly. Moreover, the larger cover thickness and the smaller diameter of the steel bar within a certain range are beneficial to prolonging the time-to-cracking.

Modeling the Amount of Steel Corrosion at the Cracking of Concrete Cover

State-of-art of corrosion-induced cracking of reinforced concrete structures

Analysis on steel corrosion at the cracking of concrete

Experimental Study and Analytical Model of Concrete Cover Spalling Induced by Steel Corrosion

Analytical model for critical corrosion level of reinforcements to cause the cracking of concrete cover

Experimental Investigation of Corrosion-Induced Cover Cracking in Reinforced Concrete Structures

Analysis on the Cracking of Concrete Cover Due to Rebar Corrosion

Modelling the corrosion mechanism of steel bars in chloride-contaminated concrete with transverse cracks

Prediction of Corrosion-Induced Concrete Cracking under External Loading and Stirrup Constraint

Modeling of Time to Corrosion-Induced Cover Cracking in Reinforced Concrete Structures

Cover Cracking Model in Reinforced Concrete Structures Subject to Rebar Corrosion

Damage Analysis and Cracking Model of Reinforced Concrete Structures with Rebar Corrosion

Corrosion-Induced Concrete Cracking Model Considering Corrosion-Filled Paste

Reinforcement Corrosion-Induced Cover Cracking and Its Time Prediction for Reinforced Concrete Structures

Numerical-based method for calculating reinforcement corrosion at concrete cover cracking due to corrosion

Crack shape and rust distribution in corrosion-induced cracking concrete coupled with load

Corrosion-induced concrete cracking model considering corrosion product-filled paste at the concrete/steel interface

On the Penetration of Corrosion Products from Reinforcing Steel into Concrete Due to Chloride-Induced Corrosion

Study On Distribution Of Steel Corrosion Products In Concrete Structures

Prediction of Corrosion-Induced Crack Width of Corroded Reinforced Concrete Structures

Fracture Model for Predicting Concrete Cover-Cracking Induced by Steel Corrosion Based on Interface Bond State