Abstract:The corrosion of steel bars significantly influences the safety running of concrete bridges. The current bridge design code always ignores the changes in mechanical properties of the materials during their service life which results in an overestimation of the seismic capacity of concrete bridges Therefore, a hysteretic constitutive model that considers the influence of reinforcement corrosion is necessary. This study established a probability-based model for the mechanical property degradation of corroded steel bars using statistical analysis to estimate the mechanical properties under specific corrosion rates. The validity of the proposed degradation model was verified by a series of monotonic tensile tests on corroded steel bars. Moreover, a constitutive model of corroded steel bars based on the Reinforcing Steel Model in OpenSees was obtained. This model considers the influence of corrosion on the slenderness ratio, yield strength, ultimate strength, and elongation. A comparison with the experimental data demonstrated the accuracy of the proposed model. The proposed model is straightforward because its parameters can be predicted using existing research data. The proposed model can provide a basis for the seismic performance evaluation of corroded reinforced concrete (RC) members.

Study On Modulus Of Rust Applied In Steel Corrosion Induced Concrete Cracking Model

Experimental Study of the Modulus of Steel Corrosion in a Concrete Port

Probability-Based Performance Degradation Model and Constitutive Model for the Buckling Behavior of Corroded Steel Bars

State-of-art of corrosion-induced cracking of reinforced concrete structures

Crack shape and rust distribution in corrosion-induced cracking concrete

Crack shape and rust distribution in corrosion-induced cracking concrete coupled with load

Study On Distribution Of Steel Corrosion Products In Concrete Structures

Composition and expansion coefficient of rust based on X-ray diffraction and thermal analysis

Critical thickness of rust layer at inner and out surface cracking of concrete cover in reinforced concrete structures

Corrosion-Induced Cracking Propagation Of Rc Beams Subjected To Different Corrosion Methods And Load Levels

Cover Cracking Model in Reinforced Concrete Structures Subject to Rebar Corrosion

Analysis on steel corrosion at the cracking of concrete

Bond Strength Evaluation of Corroded Steel Bars Via the Surface Crack Width Induced by Reinforcement Corrosion

Distribution of millscale on corroded steel bars and penetration of steel corrosion products in concrete

Modeling the Amount of Steel Corrosion at the Cracking of Concrete Cover

Behavior Of Rust Expansion Cracking Of Concrete Deduced By Equivalent Corrosion Products Of Steel Bar

Experimental Investigation of Corrosion-Induced Cover Cracking in Reinforced Concrete Structures

Corrosion-induced concrete cracking model considering corrosion product-filled paste at the concrete/steel interface

Damage Analysis and Cracking Model of Reinforced Concrete Structures with Rebar Corrosion

Determination of rust formation to cracking at the steel–concrete interface by corrosion of steel in concrete

Mill Scale and Corrosion Layer at Concrete Surface Cracking