Abstract:The corrosion of steel bars in reinforced concrete structures induces concrete cover cracking and leads to reduction in steel-concrete bond strength. In the present study, a series of pull-out tests were carried out to investigate the potential correlations between corrosion level, surface crack width, and bond strength. The main variables are corrosion level, concrete cover depth, and spacing of stirrups. The test results indicate that the surface crack width is closely linked to the corrosion level of the tensile steel bar, and the crack propagation can be divided into three stages. It is further revealed that the bond strength decreases exponentially with the surface crack width. Based on the test results, an empirical model for estimating the bond strength using the surface crack width is formulated, which considers the pronounced limiting effect of stirrups on the bond degradation. The model is further improved by incorporating the adverse effect of the corrosion of stirrups according to the previous investigations. Comparison with existing experimental database in the literature proves that the proposed models are able to realistically predict the bond strength of corroded steel bars. (C) 2017 Published by Elsevier Ltd.

Critical thickness of rust layer at inner and out surface cracking of concrete cover in reinforced concrete structures

Mill Scale and Corrosion Layer at Concrete Surface Cracking

Crack shape and rust distribution in corrosion-induced cracking concrete

Study On Distribution Of Steel Corrosion Products In Concrete Structures

Distribution of millscale on corroded steel bars and penetration of steel corrosion products in concrete

Study On Modulus Of Rust Applied In Steel Corrosion Induced Concrete Cracking Model

State-of-art of corrosion-induced cracking of reinforced concrete structures

Applicability Discussion for Multi-Peak Gaussian Model of Corrosion Layer at Steel/concrete Interfaces

Crack shape and rust distribution in corrosion-induced cracking concrete coupled with load

Bond Strength Evaluation of Corroded Steel Bars Via the Surface Crack Width Induced by Reinforcement Corrosion

Analysis on steel corrosion at the cracking of concrete

Cover Cracking Model in Reinforced Concrete Structures Subject to Rebar Corrosion

Prediction of Corrosion-Induced Crack Width of Corroded Reinforced Concrete Structures

Rust Distribution And Corrosion-Induced Cracking Patterns Of Corner Located Rebar In Concrete Cover

Non-uniform distribution of rust layer around steel bar in concrete

Analytical model for critical corrosion level of reinforcements to cause the cracking of concrete cover

Experimental Investigation of Corrosion-Induced Cover Cracking in Reinforced Concrete Structures

Modeling the Amount of Steel Corrosion at the Cracking of Concrete Cover

Thickness of the corrosion-filled paste and the corrosion layer at steel/concrete interface

Experimental Study of the Modulus of Steel Corrosion in a Concrete Port

Corrosion Ratio of Reinforcement Bar in Reinforced Concrete Construction at the Moment of Cracking Due to Corrosion Expansion