Abstract:Rare-earth-doped SiAlON and Si3N4 materials from aluminosilicate starting materials have been reported to show superior photoluminescence (PL) properties. Three different starting materials, including pulverized coal furnace fly ash, diatomite and raw illite, were used for synthesis of nitride materials. The phase and morphology evolution of these products were carefully monitored at the low temperature range of 1350 °C to 1450 °C by X-ray diffraction (XRD), scanning electronic microscopy (SEM) and Fourier-transform infrared spectroscopy (FT-IR). The PL properties of Eu-doped nitride products were also comparatively characterized. The results show that the type of starting material affects the phase composition and the photoluminescence properties of products. The existence of aluminum and alkali metals could effectively promote nitridation reactions. Aluminum in the starting materials led to the formation of different aluminum-rich nitride phases. Thus, β-SiAlON could be achieved at a much lower temperature (1350 °C) using raw illite or fly ash containing the proper amount of aluminum. Additionally, excess aluminum led to the formation of corundum and 15R-SiAlON. The products from pulverized coal furnace fly ash had more prismatic particles, and the products from diatomite had more fibrous particles. With the progress of the nitridation process, the fibers were increased, becoming longer and straighter, and the prismatic particles were more obvious. The presence of aluminum in the starting materials led to a blue shift in the photoluminescence spectrum.

Phases transformation of high-alumina fly ash under carbothermal reduction and nitridation

Phase transformation of high aluminium fly ash in carbothermal reduction–nitridation at high temperatures

Synthesis of Sialon-Mullite Composites Using Fly Ash by Carbon-Thermal Reduction Nitridation

Synthesis of Sialon Powders from Aluminium Dross and Fly Ashes

Preparation of Fly Ash-Based Porous Ceramic with Alumina as the Pore-Forming Agent

Preparation of Β-Sialon from Fly Ash by Carbothermal Reduction-Nitridation Reaction

Preparation and Characterization of Β-Sialon Ceramics from High Aluminium Fly Ash Via Carbothermal Reduction-Nitridation

Synthesis of Fe-Sialon Composites Using High Alumina Coal Gangue by Carbothermal Nitridation

The Preparation of Β-Sialon Powder from High-Alumina Fly Ash: an Experimental Study

Dilithium Dialuminium Trisilicate Crystalline Phase Prepared from Coal Fly Ash

A Study on the Preparation of the Sialon Powder with Fly Ash by the Silicon Thermal Reduetion-nitridation Method

Carbothermal Reduction Nitridation of Fly Ash, Diatomite and Raw Illite: Formation of Nitride Powders with Different Morphology and Photoluminescence Properties

Preparation of Sialon Using Fly Ash with High Content of Al2O3

The Carbon Environment Effects on Phase Composition and Photoluminescence Properties of Β-Sialon Multiphase Materials Prepared from Fly Ash Acid Slag

Effects of Sodium Carbonate and Sodium Chloride Additives on Alkaline Fusion of Coal Fly Ash

Study on Synthesizing Diphase Sialon from Lower Al2O3 Bauxite by Carbothermal Reduction-Nitridation

Preparation of Sialon/Si3N4-SiC Composite Refractories Using Kyanite Tailings

Fabrication and properties of Al 2O 3-SiC/Sialon composite refractories

Preparation of Sialon Using Fly Ash with High Content of Al<sub>2</sub>O<sub>3</sub>

Preparation of Sialon/Si<sub>3</sub>N<sub>4</sub>-SiC Composite Refractories Using Kyanite Tailings

Synthesis of Rod-Like Α-Sialon by Carbothermal Reduction-Nitridation