Preparation of Sialon/Si<sub>3</sub>N<sub>4</sub>-SiC Composite Refractories Using Kyanite Tailings

Ming Hao Fang,Zhao Hui Huang,Yan Gai Liu,Xin Min,Li Na Zhang
DOI: https://doi.org/10.4028/www.scientific.net/kem.697.467
2016-01-01
Key Engineering Materials
Abstract:Sialon-SiC composite powders were synthesized from kyanite tailings through the carbothermal reduction nitridation (CRN) technique. Using Sialon-SiC composites to substitute Si3N4 composites via the CRN technique synthesize Sialon/Si3N4-SiC composite refractories. The phase composition, cross section morphology, and the substituent amount of Sialon-SiC composites impact on refractories mechanical properties were investigated, respectively. The optimized synthesis temperature for the CRN reaction was found to be 1550 °C for 4 h with the excess carbon 20%. The substituent amount of Sialon-SiC was 25%, the mechanical properties of Sialon/Si3N4-SiC composite refractories reached optimal performance, which bending strength value was 41.8 MPa and compression strength value was 61.6 MPa.
What problem does this paper attempt to address?