Abstract:Sialon-Ti(N,C) composites were synthesized using pyrophyllite, rutile and coke powers as raw materials via carbothermal reduction-nitridation reaction. Phase composition, microstructure and micro-area element of the synthesized resultant were analyzed by X-ray diffractometer, scanning electron microscope and energy dispersive spectrometer. The effects of synthesis temperature and carbon addition content on phase compositions and mierostructure of the resultants were investigated. The results showed that the main phases of the samples which were composed of pyrophyllite and rutile with a mass ratio of 4:1, with addition of 50% excessive carbon, synthesized at 1 500 ℃ were β-sialon, 15R-sialon, TiN0.7C0.3, corundum, and a little β-SIC. Content of β-sialon and TiN0.7C0.3 increased with the increase of the synthesis temperature from 1 400 ℃ to 1 550 ℃. The content of carbon addition had an important influence on phase composition when the samples were synthesized at same temperature. It was beneficial for synthesizing sialon-TiCN,C) composite material when 50% excessive carbon was added in the samples. O'-sialon and Si2N20 will appear in resultants while the addition of carbon content was small, but β-sialon will transform to 15R-sialon while too much carbon added in the samples.The grain size of TiN0.TC0.3 crystal in sialon-Ti(N,C) composites was about 200 nm when 50% excessive carbon added in sample and synthesized at 1 500 ℃.

Synthesis of Fe-Sialon Composites Using High Alumina Coal Gangue by Carbothermal Nitridation

In-Situ Synthesis of (O′+β)-Sialon/mullite Composite Materials from Coal Gangue

Synthesis of Sialon-Mullite Composites Using Fly Ash by Carbon-Thermal Reduction Nitridation

Facile and Economical Preparation of SiAlON-Based Composites Using Coal Gangue: from Fundamental to Industrial Application

Phases transformation of high-alumina fly ash under carbothermal reduction and nitridation

Preparation of Sialon Using Fly Ash with High Content of Al2O3

Synthesis of Sialon-Ti(N,C) Composites Via Carbothermal Reduction-Nitridation from Pyrophyllite and Rutile

Fabrication and properties of Al 2O 3-SiC/Sialon composite refractories

In‐situ synthesis of 15R‐Sialon from Al‐Si 3 N 4 ‐Al 2 O 3 composite at 1500°C via liquid‐phase sintering

Effect of Alumina Contents on the Synthesis of ZrN-Sialon from Zircon

Synthesis of Β-Sialon/ti(c,n) Composites Using Low and Middle Grade Bauxite and Ilmenite by Carbothermal Reduction-Nitridation

Preparation of Sialon Using Fly Ash with High Content of Al<sub>2</sub>O<sub>3</sub>

Synthesis of Sialon Powders from Aluminium Dross and Fly Ashes

Synthesis of Sialon-SiC Composites from Kyanite Tailings by Carbothermal Reduction Nitridation

Synthesis of β-SiAlON-SiC composites from coal gangue based β-SiAlON

Preparation of Sialon/Si3N4-SiC Composite Refractories Using Kyanite Tailings

Study on Synthesizing Diphase Sialon from Lower Al2O3 Bauxite by Carbothermal Reduction-Nitridation

Preparation of β-Sialon /SiC composite powder by carbothermal reaction of coal-mine schist

Fe–Sialon–Ti(C,N) Composites from Carbothermal Reduction–nitridation of Low-Priced Minerals and Their Application in Taphole Clay Refractories

Preparation of Sialon/Si<sub>3</sub>N<sub>4</sub>-SiC Composite Refractories Using Kyanite Tailings

Fabrication and Properties of Al<sub>2</sub>O<sub>3</sub>-SiC/Sialon Composite Refractories