Abstract:Sialon-Ti(N,C) composites were synthesized using pyrophyllite, rutile and coke powers as raw materials via carbothermal reduction-nitridation reaction. Phase composition, microstructure and micro-area element of the synthesized resultant were analyzed by X-ray diffractometer, scanning electron microscope and energy dispersive spectrometer. The effects of synthesis temperature and carbon addition content on phase compositions and mierostructure of the resultants were investigated. The results showed that the main phases of the samples which were composed of pyrophyllite and rutile with a mass ratio of 4:1, with addition of 50% excessive carbon, synthesized at 1 500 ℃ were β-sialon, 15R-sialon, TiN0.7C0.3, corundum, and a little β-SIC. Content of β-sialon and TiN0.7C0.3 increased with the increase of the synthesis temperature from 1 400 ℃ to 1 550 ℃. The content of carbon addition had an important influence on phase composition when the samples were synthesized at same temperature. It was beneficial for synthesizing sialon-TiCN,C) composite material when 50% excessive carbon was added in the samples. O'-sialon and Si2N20 will appear in resultants while the addition of carbon content was small, but β-sialon will transform to 15R-sialon while too much carbon added in the samples.The grain size of TiN0.TC0.3 crystal in sialon-Ti(N,C) composites was about 200 nm when 50% excessive carbon added in sample and synthesized at 1 500 ℃.

Study on Synthesizing Diphase Sialon from Lower Al2O3 Bauxite by Carbothermal Reduction-Nitridation

Synthesis of Β-Sialon/ti(c,n) Composites Using Low and Middle Grade Bauxite and Ilmenite by Carbothermal Reduction-Nitridation

Synthesis of Rod-Like Α-Sialon by Carbothermal Reduction-Nitridation

Preparation of Β-Sialon from Fly Ash by Carbothermal Reduction-Nitridation Reaction

Effect of Reaction Temperature on the Synthesis of Β-Sialon/ti(c, N) Composites from Low Grade Bauxite and Ilmenite

Synthesis of α-Sialon by High Temperature Nitridation Reaction

Phase Behavior Analysis of Low-Grade Bauxite and Rutile by Carbothermal Reduction-Nitridation

Synthesis of alpha-Sialon by High Temperature Nitridation Reaction

Synthesis of Sialon Powders from Aluminium Dross and Fly Ashes

Synthesis of Prismatic Β-Sialon from the Precursor of SBA-15 Incorporated with Al(NO3)3 Via Carbothermal Reduction Nitridation

Fabrication and properties of Al 2O 3-SiC/Sialon composite refractories

Effect of Alumina Contents on the Synthesis of ZrN-Sialon from Zircon

Phases transformation of high-alumina fly ash under carbothermal reduction and nitridation

Synthesis of Fe-Sialon Composites Using High Alumina Coal Gangue by Carbothermal Nitridation

Preparation and Characterization of Β-Sialon Ceramics from High Aluminium Fly Ash Via Carbothermal Reduction-Nitridation

Synthesis And Characterization Of Single-Crystalline Phase Li-Alpha-Sialon

Synthesis of Β-Sialon/ti(c, N) Powders from Mineral Waste Residue Via Carbothermal Reduction Nitridation

Synthesis of Sialon-Ti(N,C) Composites Via Carbothermal Reduction-Nitridation from Pyrophyllite and Rutile

Preparation and formation mechanism of elongated (Ca, Dy)-α-sialon powder via carbothermal reduction and nitridation

Preparation And Formation Mechanism Of Elongated (Ca,Dy)-Alpha-Sialon Powder Via Carbothermal Reduction And Nitridation

Preparation of Sialon Using Fly Ash with High Content of Al<sub>2</sub>O<sub>3</sub>