Effect of Reaction Temperature on the Synthesis of Β-Sialon/ti(c, N) Composites from Low Grade Bauxite and Ilmenite

SHEN Jian-xin,YANG De-xin,CHEN Yong-bo,WANG Bao-chen,LIU Yan-gai

2013-01-01

Abstract:β-Sialon/Ti(C,N) composites were prepared by carbothermal reduction-nitridation reaction(CRN) using low grade bauxite and ilmenite as starting materials at different temperatures,the ratio of ilmenite and bauxite was 50∶ 50,the composition and microstructure of products were studied by X-ray diffraction(XRD) and scanning electron microscope(SEM).The results showed that the best reaction temperature was 1250 ℃,because the phases of products mainly were β-Sialon(z=3),Ti(C,N) and Al2O3 at that reaction temperature.When the sintering temperature was under that temperature,the products still had the phase of mullite,which illustrated the reaction was not complete.When the reaction temperature was higher than the best reaction temperature,the main product was AlN.The microstructure of β-Sialon was prismatic;the shape of AlN was lamellar and that of iron was globular.