Abstract:Sialon-Ti(N,C) composites were synthesized using pyrophyllite, rutile and coke powers as raw materials via carbothermal reduction-nitridation reaction. Phase composition, microstructure and micro-area element of the synthesized resultant were analyzed by X-ray diffractometer, scanning electron microscope and energy dispersive spectrometer. The effects of synthesis temperature and carbon addition content on phase compositions and mierostructure of the resultants were investigated. The results showed that the main phases of the samples which were composed of pyrophyllite and rutile with a mass ratio of 4:1, with addition of 50% excessive carbon, synthesized at 1 500 ℃ were β-sialon, 15R-sialon, TiN0.7C0.3, corundum, and a little β-SIC. Content of β-sialon and TiN0.7C0.3 increased with the increase of the synthesis temperature from 1 400 ℃ to 1 550 ℃. The content of carbon addition had an important influence on phase composition when the samples were synthesized at same temperature. It was beneficial for synthesizing sialon-TiCN,C) composite material when 50% excessive carbon was added in the samples. O'-sialon and Si2N20 will appear in resultants while the addition of carbon content was small, but β-sialon will transform to 15R-sialon while too much carbon added in the samples.The grain size of TiN0.TC0.3 crystal in sialon-Ti(N,C) composites was about 200 nm when 50% excessive carbon added in sample and synthesized at 1 500 ℃.

Synthesis of Rod-Like Α-Sialon by Carbothermal Reduction-Nitridation

Synthesis of α-Sialon by High Temperature Nitridation Reaction

Synthesis of alpha-Sialon by High Temperature Nitridation Reaction

Preparation of Β-Sialon from Fly Ash by Carbothermal Reduction-Nitridation Reaction

Study on Synthesizing Diphase Sialon from Lower Al2O3 Bauxite by Carbothermal Reduction-Nitridation

Effect of Alumina Contents on the Synthesis of ZrN-Sialon from Zircon

Synthesis of ZrN-sialon composites from zircon and alumina by carbothermal reduction-nitridation

Combustion Synthesis of Rod-Like Α-Sialon Seed Crystals

Synthesis of Β-Sialon/ti(c,n) Composites Using Low and Middle Grade Bauxite and Ilmenite by Carbothermal Reduction-Nitridation

Synthesis of Sialon Powders from Aluminium Dross and Fly Ashes

In‐situ synthesis of 15R‐Sialon from Al‐Si 3 N 4 ‐Al 2 O 3 composite at 1500°C via liquid‐phase sintering

Novel rod-like yttrium α-sialon crystalline powders prepared by combustion synthesis

Phase transformation of high aluminium fly ash in carbothermal reduction–nitridation at high temperatures

Synthesis of Environment-Friendly Sialon/SiC Multiphase Ceramics from Cheap Nonmetallic Resources

Synthesis of Sialon-Ti(N,C) Composites Via Carbothermal Reduction-Nitridation from Pyrophyllite and Rutile

Preparation and formation mechanism of elongated (Ca, Dy)-α-sialon powder via carbothermal reduction and nitridation

Synthesis of Sialon-SiC Composites from Kyanite Tailings by Carbothermal Reduction Nitridation

Synthesis and characterization of single-crystalline phase Li-α-Sialon

Preparation And Formation Mechanism Of Elongated (Ca,Dy)-Alpha-Sialon Powder Via Carbothermal Reduction And Nitridation

Synthesis of Prismatic Β-Sialon from the Precursor of SBA-15 Incorporated with Al(NO3)3 Via Carbothermal Reduction Nitridation

Combustion synthesis of rod-like Yb alpha-sialon powders