Abstract:The mechanically-alloyed amorphous 2Si-B-3C-N powder was hot pressed at 1900°C for 30mins in argon. A small amount (5mol.%) of AlN and ZrO2 was added to investigate their effect on the sintering process, microstructure and properties of the 2Si-B-3C-N ceramic. XRD, SEM, TEM and property testing results show that, the addition of AlN or ZrO2 promotes the sintering process of the 2Si-B-3C-N composite powder, accelerates the crystallization and grain growth, and improves the density and mechanical properties of the prepared ceramic. Under an axial pressure of 80MPa and a gas pressure of 8bar, significant densification occurs to the 2Si-B-3C-N ceramic free from any additives just when the temperature is higher than 1830°C. The addition of AlN and ZrO2 decreases this critical temperature to about 1760°C and 1730°C, respectively. As a result, for the prepared bulk ceramic, the average grain size is increased from 80nm to 200nm and 250nm, the relative density is enhanced from 88.7% to 96.9% and 97.7%, and the bending strength is improved from 331MPa to 416MPa and 575MPa, respectively. Careful investigation reveals that in the prepared bulk ceramic, AlN forms solid solution with SiC, and ZrO2 exists in the form of t-ZrO2 and m-ZrO2 nanocrystals. Thus, the addition of AlN and ZrO2 may facilitate the atomic diffusion, the grain growth and the densification process of the 2Si-B-3C-N ceramic in difficult ways.

Effect of Alumina Contents on the Synthesis of ZrN-Sialon from Zircon

Synthesis of ZrN-sialon composites from zircon and alumina by carbothermal reduction-nitridation

Effects of carbon coke additions on synthesis of ZrN-SiAlON from zircon and alumina by carbothermal reduction nitridation process

In‐situ synthesis of 15R‐Sialon from Al‐Si 3 N 4 ‐Al 2 O 3 composite at 1500°C via liquid‐phase sintering

Synthesis of Rod-Like Α-Sialon by Carbothermal Reduction-Nitridation

Influence of Sintering Temperature on Phase Behavior of Products from Rutile and Quartz by Aluminothermic Reduction Nitridation

Carbothermal/aluminothermic Reduction Nitridation Synthesis of ZrN–SiAlON Refractory Composites from Zircon and Bauxite: a Comparative Study of the Reduction Effect of Reducers

Synthesis of Fe-Sialon Composites Using High Alumina Coal Gangue by Carbothermal Nitridation

Fabrication and properties of Al 2O 3-SiC/Sialon composite refractories

Effect of ZrN-Sialon Composite Powder on Properties of Al2O3-C Refractory

Study on Synthesizing Diphase Sialon from Lower Al2O3 Bauxite by Carbothermal Reduction-Nitridation

Effect of AlN and ZrO2 on the Microstructure and Property of the 2Si-B-3c-n Ceramic

Effect of Reaction Temperature on the Synthesis of Β-Sialon/ti(c, N) Composites from Low Grade Bauxite and Ilmenite

Synthesis of Prismatic Β-Sialon from the Precursor of SBA-15 Incorporated with Al(NO3)3 Via Carbothermal Reduction Nitridation

Synthesis of α-Sialon by High Temperature Nitridation Reaction

Influence of Aluminum Contents on Phase Behavior and Properties of TiN-Sialon-Corundum Composites by Aluminothermic Reduction Nitridation

Synthesis of alpha-Sialon by High Temperature Nitridation Reaction

Synthesis of Β-Sialon/ti(c,n) Composites Using Low and Middle Grade Bauxite and Ilmenite by Carbothermal Reduction-Nitridation

Phases transformation of high-alumina fly ash under carbothermal reduction and nitridation

Synthesis of ZrN–Si3N4 composite powders from zircon and quartz by carbothermal reduction and nitridation

Fabrication and Properties of Al<sub>2</sub>O<sub>3</sub>-SiC/Sialon Composite Refractories