Effects of carbon coke additions on synthesis of ZrN-SiAlON from zircon and alumina by carbothermal reduction nitridation process

Li Yuetong,Xu Youguo,Minghao Fang,Liu Yangai,Zhaohui Huang

2012-01-01

Refractories

Abstract:Natural zircon,alumina and carbon coke were used as starting materials for the preparation of ZrN-SiAlON composite by carbonthermal reduction nitridation.The mass ratio of zircon and industrial alumina was designed according to equation 3Al2O3+6ZrSiO4+27C+8N2 6ZrN+2Si3Al3O3N5+27CO.The additions of carbon coke were stoichiometric amount,excess 5 mass%,excess 10 mass% and excess 20 mass%,respectively.After ball-milling,molding,drying and firing at 1 500,1 550 and 1 600 ℃ for 4 h under flowing nitrogen followed by natural cooling down to room temperature,respectively,the phase compositions and microstructure of the synthetic products were investigated.The results show that:(1)increasing coke content is beneficial to the formation of ZrN at 1 500 ℃;(2)when the firing temperature is 1 550 ℃,there is 15R-SiAl4O2N4(SiAl4O2N4) in the products with excess 20 mass% carbon coke addition;(3)when the firing temperature is 1 600 ℃,there is 15R-SiAl4O2N4 in the products with stoichiometric or excess 5 mass% carbon coke addition and there is 12H-SiAl4O2N4(SiAl5O2N5) in the products with excess 10 mass% or excess 20 mass% carbon coke addition.