Abstract:The composite ceramics between Al 2 O 3 (6 mol%MgO) and ZrO 2 (4 mol%Y 2 O 3 ) were prepared in the Al 2 O 3 (6 mol%MgO added: ZrO 2 (4 mol%Y 2 O 3 added) ratios of 20:80, 35:65, 50:50, 65:35 and 80:20. All of samples were sintered using two stage sintering routes with the first temperature (T 1 ) at 1600 °C for 30 min and the second temperature (T 2 ) at 1450 °C for 5 h. The physical properties were characterized from percentage of shrinkage and bulk density. It can be found their tend to decrease with Al 2 O 3 (6 mol%MgO) content increase. XRD patterns were showed combination main phase of rhombohedral of Al 2 O 3 and monoclinic, cubic, tetragonal of ZrO 2 . Rietveld refinement were used to calculate the percentage of phase composition. All of samples were revealed weight percentage of main composition as m -ZrO 2 c -ZrO 2 t -ZrO 2 and r - Al 2 O 3 in different ratios. It can be found, sample with more content of ZrO 2 was showed higher weight percentage of c -ZrO 2 . The high intensity of Al 2 O 3 peak was appeared from sample with high Al 2 O 3 concentration. SEM micrographs reveal morphology of grain such as grain shape and size of grains. The average grain size value is between 0.81 and 1.07 μm and the size of grain tend to increase with high Al 2 O 3 content. EDX technique were analyzed element compositions of Al 2 O 3 (6 mol%MgO): ZrO 2 (4 mol%Y 2 O 3 ) and EDX spectra were showed wt.% element of Al, Zr, O Y and Mg which is confirmed molecular formular. Moreover, EDX method is identified square shape of Al 2 O 3 (6 mol%MgO) and round shape of ZrO 2 (4 mol%Y 2 O 3 ). The mechanical properties were measured by Vickers and Knoop hardness that were used for calculating the fracture toughness value. It can be found that the optimum mechanical properties were obtained from composite ceramic of 0.35Al 2 O 3 (6 mol%MgO): 0.65ZrO 2 (4 mol%Y 2 O 3 ) which is showed the highest of fracture toughness value about 0.38 GPa.m 1/2 .

Effect of ZrN-Sialon Composite Powder on Properties of Al2O3-C Refractory

Effect of Al2O3 addition on properties of non-sintered SiC–Si3N4 composite refractory materials

Effects of ZrB2 on Mechanical Properties of Al2O3-ZrB2-SiC Composite Ceramics at Room Temperature

Microstructure, phase evolution, mechanical properties and slag corrosion resistance of ZrO2 reinforced Al2O3–Cr2O3 composites

Microstructure and mechanical properties of CaAl12O19 reinforced Al2O3-Cr2O3 composites

Effects of Cr2O3 Content on Microstructure and Mechanical Properties of Al2O3 Matrix Composites

The Effect of Nano-Al<sub>2</sub>O<sub>3</sub> on Sintering Behavior and Mechanical Property of ZrO<sub>2</sub> Ceramics

The Effect of Nano-Al2O3 on Sintering Behavior and Mechanical Property of ZrO2 Ceramics

Effect of Zr2Al4C5 Content on the Mechanical Properties and Oxidation Behavior of ZrB2-SiC-Zr2Al4C5 Ceramics

Enhanced thermal shock resistance of BN-based composites sintered by hot-pressing with the introduction of nano oxides

Enhanced performance of low-carbon MgO–C refractories with nano-sized ZrO2–Al2O3 composite powder

Effects of ZrC content on the microstructure and mechanical property of ZrC/ZTA composites consolidated by hot pressing

Preparation and thermal shock resistance investigation of ZTA-La 2 O 3 composite ceramics for porous medium combustion materials

SiC and ZrN Nano-Particulate Reinforced AlON Composites: Preparation, Mechanical Properties and Toughening Mechanisms

High-temperature performance in Al2O3–Cr2O3 refractories: Effect of Al2TiO5

Effects of Composite Systems on Sintering Properties of Aluminum Oxide Ceramics

Preparation and Characterization of Alumina Zirconia Composite Ceramics

Effect of silicon powder-modified tabular alumina aggregates on the mechanical properties and microstructures of carbon-bonded alumina refractories

Fabrication and Characterization of ZrO_2/SiC Composite Materials

Improved thermal shock resistance of low-carbon Al2O3–C refractories fabricated with C/MgAl2O4 composite powders

Effect of preset interfacial ZrB 2 particles on the microstructure and properties of C/C-AlSi composites