Abstract:Bauxite based β-SiAION (designed value of z is 2) bonded corundum-SiC composites were prepared by nitridation at 1500 °C for 5 h, using fused corundum(≤0.088 mm, ≤l mm and 3~1 mm), SiC(3~1 mm), Al2O3 micropowder, bauxite, Al and Si powders as starting materials. The influence of SiC content (0,10%, 20% ,30% ,40%), addition of Al2O3 micropowder (0,1% ,3% ,5% ,7%) and theoretical amount of the resultant β-SiAION (15% ,20%,25%) on the bulk density, apparent porosity and cold strength, and the relationship between HMOR of the composites with different β-SiAION contents and temperature(400 ~ 1400 °C) were also investigated. The crystal phase and microstructure of composites were analyzed by XRD,SEM and EDS. Results showed that: 1) With the increase of SiC content, the bulk density decreased, but the apparent porosity and cold strength increased. The comprehensive properties were proved to be better while 30% SiC was added. 2) With the increase of Al2O3 micropowder, the bulk density increased, the apparent porosity decreased. The eligible addition of alumina powder is 3%. 3) The HMOR increased to maximum with the temperature rising up to 1000 °C and decreased at above 1000 °C. However, at 1400 °C, the HMOR of composites with 20% and 25% β-SiAION was still higher than its CMOR. The reason is that the interlocking columnar β-SiAION crystals are filled into the interstice between the corundum and SiC framework, bringing strengthening and plasticizing effects.

Fabrication and Properties of Al<sub>2</sub>O<sub>3</sub>-SiC/Sialon Composite Refractories

Fabrication and properties of Al 2O 3-SiC/Sialon composite refractories

Preparation of Sialon/Si<sub>3</sub>N<sub>4</sub>-SiC Composite Refractories Using Kyanite Tailings

Sintering Behavior, Microstructure and Mechanical Properties of Various Fluorine-Containing Y-SiAlON Glass-Ceramics

Preparation of Sialon/Si3N4-SiC Composite Refractories Using Kyanite Tailings

Preparation And Properties Of Sintering-Free Low Density Si3n4/Sic Composite Refractory

Preparation and Characterization of Β-Sialon Ceramics from High Aluminium Fly Ash Via Carbothermal Reduction-Nitridation

Β-Sialon -Al2o3-sic Composite Refractories

Effect of Silicon Addition on Mechanical Properties of Mullite-Sic Composite Refractories

Effects of Silica Sol/Phenolic Resin on Properties of Unfired Al2O3-β-Sialon/Ti(C,N)/SiC-C Composite Refractory Material

Preparation and Properties of SiC Refractories Via Carbonization-Nitridation Reaction

Preparation and properties of bauxite based β-SiAION bonded corundum-SiC composites

Fabrication of Si3N4 ceramics with improved thermal conductivity by carbothermal reduction and two‐step sintering

Hot strength and microstructure of β-sialon-Al2O3-SiC composites

Effect of Al 2 O 3 addition on properties of non-sintered SiC–Si 3 N 4 composite refractory materials

Fabrication and mechanical properties of α-Al2O3/β-Al2O3/Al/Si composites by liquid displacement reaction

Study on Fabrication of Al2O3-MgO (Spinel)-Sialon Composite Refractory

Fabrication and Properties of Si<sub>3</sub>N<sub>4</sub>-SiC-C Refractory Composites

Fabrication and Properties of SiC/mullite Composite Porous Ceramics

Effect of Al2O3 addition on properties of non-sintered SiC–Si3N4 composite refractory materials

Reaction Sintered Fe–Sialon Ceramic Composite: Processing, Characterization and High Temperature Erosion Wear Behavior

Fabrication and Properties of Al&lt;sub&gt;2&lt;/sub&gt;O&lt;sub&gt;3&lt;/sub&gt;-SiC/Sialon Composite Refractories