Abstract:During industrial and laboratory processes involving material grinding, the grinding media endure prolonged high-collision and friction environments, resulting in substantial wear. Consequently, this study adopts the hot-pressing sintering technique in powder metallurgy to prepare SiC-reinforced Fe-based wear-resistant composite grinding media, aiming to increase wear performance. For this purpose, Fe with 10 wt% SiC powders were milled for the fabrication of the composite. Then, sintering was performed by hot press at 1100 °C in a furnace. Scanning electron microscopy (SEM) and X-ray diffraction were employed to investigate the microstructures and phase of SiC-reinforced Fe-based matrix composite. Subsequently, comparative performance evaluations of the newly developed grinding media and traditional chromium-based media were conducted in terms of wear rate and grinding efficiency. The wear resistance tests revealed that the SiC-reinforced composite media displayed significantly superior wear resistance across various abrasives compared to the chromium-containing alternatives. Specifically, the composite media achieved a wear rate reduction of 2.9 times against standard sand over 1 h, and 2.3 and 2.4 times against sandstone and iron slag, respectively. Moreover, extended grinding for 3 hours further enhanced these reductions to 3.1, 2.4, and 2.7 times, respectively. Additionally, efficiency assessments indicated that at a 1:1 material ratio, the composite media outperformed the chromium-containing media in grinding efficiency by 7.5%, 12.5%, and 10.3% for standard sand, sandstone, and iron slag, respectively. Further increasing the material ratio to 3:1 resulted in efficiency improvements of 7.4%, 17.5%, and 11.3%, correspondingly.

Reaction Sintered Fe–Sialon Ceramic Composite: Processing, Characterization and High Temperature Erosion Wear Behavior

Abrasive wear behavior of Sialon ceramic

Preparation and Performance Study of SiC-Reinforced Fe-Based Wear-Resistant Composite Grinding Media

Erosive Wear Behavior of Reaction Sintered Si3N4-SiCp Composite Ceramic in Liquid-Solid Flow

Interfacial characterization and erosive wear performance of zirconia toughened alumina ceramics particles reinforced high chromium white cast irons composites

Effect of Abrasive Particle Size on Anti-Abrasion Performance of Si3N4 Ceramics

Erosion behavior between CaCl2 and β-Sialon -SiC composite used for blast furnaces

Fabrication and Characterization of ZrO_2/SiC Composite Materials

Molten Aluminum-Induced Corrosion and Wear-Resistance Properties of ZrB2-Based Cermets Improved by Sintering-Temperature Manipulation

Interfacial characteristics and wear performances of iron matrix composites reinforced with zirconia-toughened alumina ceramic particles

In-situ synthesis of Fe Si phases and their effects on the properties of SiC porous ceramics

Structural characteristics and ablative behavior of C/C–ZrC–SiC composites reinforced with “Z-pins like” Zr–Si–B–C multiphase ceramic rods

Hot strength and microstructure of β-sialon-Al2O3-SiC composites

Effect of the amount of SiC particles on the microstructure, mechanical and wear properties of FeMnCoCr high entropy alloy composites

The Tribological Properties and Wear Mechanism of Copper Coated Graphite Doped Sialon Ceramic Composites at Wide Range Temperature from 25 to 800 °C

Effect of SiC on the anti-ablation resistance and flexural strength of (Hf-Ta-Zr)C-C/C composites

Sn-containing Si3N4-based composites for adaptive excellent friction and wear in a wide temperature range

Erosive Wear Performance and Mechanism of Engineering Ceramic Materials

Erosion behavior between CaCl2 and beta-sialon-SiC composite used for blast furnaces

Microstructure and Mechanical Properties of Hot-Pressed Al2O3–mullite–ZrO2–SiC Composites

Temperature‐dependent mechanical and oxidation behavior of in‐situ formed ZrN/ZrO2‐containing Si3N4‐based composite