Abstract:Electroless nickel composite coatings have the potential for high-temperature tribological applications, and a combination of high wear resistance and low friction factor is one of the desirable solutions but still a tricky problem. The addition of self-lubricating WS2 and hard Si3N4 nanoparticles to the Ni-P coatings is expected to obtain good high-temperature tribological performance. In this work, Ni-P-Si3N4-WS2 composite coatings with various contents of WS2 nanoparticles were prepared using electroless plating and subsequently annealed at 400 °C in an inert atmosphere. The tribological properties of the coatings were evaluated using a ball-on-disc wear instrument at operating temperatures from 25 to 600 °C. The microstructure, chemical composition, and surface morphology of the coatings were characterized by X-ray diffractometry (XRD), energy disperse spectroscopy (EDS), and scanning electron microscopy (SEM). Upon increasing the WS2 dosage in the bath, the WS2 content in the coating increased and the micro-hardness of the as-plated coating increased from 539 to 717 HV. After heat treatment, the coating underwent a crystallization process, and the hardness increased from 878 to 1094 HV. The main wear mechanism of the coating changed from adhesive wear in the as-plated state to abrasive wear in the annealed state. The annealed Ni-P-Si3N4-WS2 coating with a WS2 dosage of 2.5 g/L in the bath exhibited excellent mechanical properties, with a hardness of 10.9 GPa, a friction coefficient of ~0.51, and a wear rate of 8.4 × 10−15 m3N−1×m−1 at room temperature, and maintained optimal performance at high temperatures. At operating temperatures of 200, 400, and 600 °C, the form of wear was adhesive wear for coatings with a WS2 dosage < 1.5 g/L and abrasive wear for coatings with a WS2 dosage ≥ 1.5 g/L. The synergism of WS2 and Si3N4 particles refined the grains of the Ni-P matrix in as-plated coatings and obviously reduced the friction coefficient of friction pairs in annealed coatings at all operating temperatures.

Sn-containing Si3N4-based composites for adaptive excellent friction and wear in a wide temperature range

Tribological behavior of NiCrW-based self-lubricating composites against IC10 alloy under high temperature and extremely slow sliding speed

High-Temperature Friction and Wear Behavior of Nickel-Alloy Matrix Composites with the Addition of Molybdate

Effects of Temperature and Normal Load on Tribological Behavior of Nickel-Based High Temperature Self-Lubricating Wear-Resistant Composite Coating

Wear Properties of NiAl Based Materials

Tribological behavior of h -BN/Al 2 O 3 self-lubricating composites in extreme environments–Part I: Lubricating behavior and ultra-low friction coefficient mechanism in air environments from room temperature to 1200 °C

High Temperature Tribological Behavior of Electroless Plating Ni-P-Si3N4-WS2 Composite Coatings

Ni/Si3N4 composite coatings and their water lubrication behaviors

Friction and wear performance of a NiAl-8 wt% serpentine-2 wt%TiC composite at high temperatures

High-Temperature Tribological Behavior of Fast-Hot-Pressed NiCr/Cr3C2-LaF3 Self-Lubrication Composite

Enhanced Elevated-Temperature Tribological Properties and Microstructure of Co-continuous Iron Foam/SiC/Al-Si Dual-Reinforced Composites Fabricated by Vacuum-Assisted Infiltration

High temperature tribological performance of nickel-based composite coatings by incorporating multiple oxides (TiO2–ZnO–MoO3)

Temperature-mediated tribological characteristics of 40CrNiMoA steel and Inconel 718 alloy during sliding against Si3N4 counterparts

High-performance TiN Reinforced Sialon Matrix Composites: A Good Combination of Excellent Toughness and Tribological Properties at a Wide Temperature Range

High temperature and room temperature tribological behaviors of in-situ carbides reinforced Ni-based composites by reactive sintering Ni and Ti2AlC precursor

Improving the tribological properties of ZrO2(Y2O3)-graphite composites at high temperature through three-dimensional continuous structure

Self-lubricating behavior caused by tribo-oxidation of Ti3SiC2/Cu composites in a wide temperature range

High temperature tribological response of Fe-2Cu-0.8C-CaF2 self-lubricating composites at high speeds

In situ preparation of a SiC–TiB2 composite and its wear fracture mechanism at high temperatures

Tribological behaviors of vacuum hot-pressed ceramic composites with enhanced cyclic oxidation and corrosion resistance

Tailoring Polyimide Composites with Low Friction and Wear at High Temperatures