Abstract:The unsatisfactory high-temperature performance of commonly used silicon carbide (SiC)-based ceramics calls for a novel approach for their reinforcement. We present the in situ preparation of a SiC-based composite with uniformly dispersed titanium boride (TiB2) particles using titanium carbide and boron carbide as raw materials. Notably, the uniform incorporation of 25 wt%TiB2 results in the SiC–TiB2 composite with excellent tribological and self-lubricating properties at high temperatures. The SiC–TiB2 composite shows a friction coefficient of 0.20 and a specific wear rate of 5.77 × 108 mm3/(N mm), which are 4.75 times and ~ 5.2 times lower than that of the bare SiC ceramic at 1000 °C, respectively. The wear mechanism of a self-mated couple of the SiC–TiB2 composite is unraveled to be the tribo-oxidization. Since intimate contact exists between the oxidizing layer and the transitional layer of the fractured surface, the friction surface possessing plastic deformation properties may transit from brittle to plastic or elastic. The "Pin Effect" exhibited by TiB2 particles in the SiC–TiB2 composite deflects the crack propagation route. Meanwhile, a change in stress distribution, a decrease in the stress intensity of slight crack frontier, and an increase in "the threshold value" of crack propagation occur. The type (I + II) and type (I + III) complex cracks in fracture mechanics propagate non-flatly in the wearing process of the self-mated couple of the SiC–TiB2 composite. Besides, a fine yield deformation zone exists on the crack tip. Consequently, the "threshold value" of crack propagation fluctuates dynamically between "upper bound value" and "lower bound value" following the change in the valid length of actual crack propagation, thus delaying the fracture of the SiC–TiB2 composite.

High-performance TiN Reinforced Sialon Matrix Composites: A Good Combination of Excellent Toughness and Tribological Properties at a Wide Temperature Range

In situ preparation of a SiC–TiB2 composite and its wear fracture mechanism at high temperatures

Synthesis and Tribological Characterization of Ti3SiC2/ZnO Composites

Tribological Behavior Of Graphene Reinforced 600 Degrees C High Temperature Titanium Alloy Matrix Composite

Effect of Temperature on Tribological Properties of Tial Based Self-Lubricating Composites

The Tribological Properties and Wear Mechanism of Copper Coated Graphite Doped Sialon Ceramic Composites at Wide Range Temperature from 25 to 800 °C

Tribological behaviors of vacuum hot-pressed ceramic composites with enhanced cyclic oxidation and corrosion resistance

High temperature and room temperature tribological behaviors of in-situ carbides reinforced Ni-based composites by reactive sintering Ni and Ti2AlC precursor

Tribological Behavior of TiC Particles Reinforced 316Lss Composite Fabricated Using Selective Laser Melting

In-situ synthesized a dual-scale Ti 2 AlC reinforced TiAl composites with superior mechanical properties

Network-Strengthened Ti-6Al-4V/(TiC+TiB) Composites: Powder Metallurgy Processing and Enhanced Tensile Properties at Elevated Temperatures

Preparation and Characterization of In Situ (TiC-TiB2)/Al-Cu-Mg-Si Composites with High Strength and Wear Resistance

Friction and wear performance of a NiAl-8 wt% serpentine-2 wt%TiC composite at high temperatures

Microstructure and tribological behaviors of laser cladded CuAlMnTi–xTiC composite coatings at elevated temperature

Study of the high-temperature mechanical properties of Al-6061/NiTi reinforced metal matrix composites

Tuning composition and microstructure by doping Ti and C for enhancing mechanical property and wear resistance of Al0.2Co1.5CrFeNi1.5Ti0.5 high entropy alloy matrix composites

Interfacial structure and wear properties of selective laser melted Ti/(TiC+TiN) composites with high content of reinforcements

Sn-containing Si3N4-based composites for adaptive excellent friction and wear in a wide temperature range

Sintering and Tribological Properties of Ti3SiC2-TiSix Composite Sintered by High-Pressure High-Temperature Technology

Properties and elevated temperature wear mechanism of pure copper and TiC/Cu nanocomposites

Sialon Tailoring Copper-Based Composite to Achieve High Strength, High Strain Integrated with Excellent Wear Resistance