Effect of Abrasive Particle Size on Anti-Abrasion Performance of Si3N4 Ceramics

Chonggao Bao,Wei Pan,Hezhuo Miao,Longhao Qi

DOI: https://doi.org/10.3321/j.issn:0253-987X.2005.11.014

2005-01-01

Abstract:Erosion resistance of Si3N4 structure ceramics was investigated using water slurry with different SiC particle sizes on a liquid-solid dual phase erosion tester with a rotation disk, and Cr15Mo3 high chromium cast iron was taken as a contrast in the test. The erosive mechanism of the test materials in slurry erosion was also discussed. The results show that the slurry erosion of Cr15Mo3 is more severe than that of Si3N4 with varying abrasive particles diameters. The erosive resistance of Si3N4 ceramics is 20 times higher than that of Cr15Mo3 cast iron. The lost volume of the test materials eroded by larger particles is larger than that by smaller ones. SEM observation reveals that there exist more abrasive and erosive pits on worn surface of Cr15Mo3 iron, compared with smooth worn surface of Si3N4, and W-shaped fault feature appears on some failure surfaces of Cr15Mo3 iron. The better erosive resistance of Si3N4 lies in its finer granular and column grains, higher density and hardness.