Hot strength and microstructure of β-sialon-Al2O3-SiC composites

Zhaohui Huang,Wei Pan,Jialin Sun,Jinxiang Wang,Yanruo Hong

2004-01-01

Abstract:Microstructures and relationships between MOR (modulus of rupture) of β-sialon-Al2O3-SiC composites and temperatures were studied. The results show that MOR of β-sialon-Al2O3-SiC composites goes up depending on increases of temperatures, and reaches the maximum value at 1200°C, and goes down slowly when the temperature is over 1200°C. This is attributed to the enhancing mechanism of decreasing of residual thermal stresses in the composites at high temperatures and protecting functions of oxidation films on the surface of specimens. Study on the microstructure of fracture surface of specimens reveals that the bonding strength between β-sialon and SiC in the composites is excellent. The intragranular fracture of SiC grains and corundum grains is dominant in some specimens. Others, micro-cracks and gaps between corundum grains and the matrix at lower temperatures can be closed by the heat expansion of corundum grains at higher temperatures, and can improve MOR of specimens at high temperatures. The fracturing style of corundum grains changes from intergranular fracture at lower temperatures to intragranular fracture at higher temperatures. Having exhibited the high compressive strength of 46 MPa to 57 MPa at 1400°C, the β-sialon-Al2O3-SiC composites deserve to be new promising advanced refractories.