Abstract:Sialon-Ti(N,C) composites were synthesized using pyrophyllite, rutile and coke powers as raw materials via carbothermal reduction-nitridation reaction. Phase composition, microstructure and micro-area element of the synthesized resultant were analyzed by X-ray diffractometer, scanning electron microscope and energy dispersive spectrometer. The effects of synthesis temperature and carbon addition content on phase compositions and mierostructure of the resultants were investigated. The results showed that the main phases of the samples which were composed of pyrophyllite and rutile with a mass ratio of 4:1, with addition of 50% excessive carbon, synthesized at 1 500 ℃ were β-sialon, 15R-sialon, TiN0.7C0.3, corundum, and a little β-SIC. Content of β-sialon and TiN0.7C0.3 increased with the increase of the synthesis temperature from 1 400 ℃ to 1 550 ℃. The content of carbon addition had an important influence on phase composition when the samples were synthesized at same temperature. It was beneficial for synthesizing sialon-TiCN,C) composite material when 50% excessive carbon was added in the samples. O'-sialon and Si2N20 will appear in resultants while the addition of carbon content was small, but β-sialon will transform to 15R-sialon while too much carbon added in the samples.The grain size of TiN0.TC0.3 crystal in sialon-Ti(N,C) composites was about 200 nm when 50% excessive carbon added in sample and synthesized at 1 500 ℃.

Synthesis of Environment-Friendly Sialon/SiC Multiphase Ceramics from Cheap Nonmetallic Resources

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

Synthesis of Sialon-SiC Composites from Kyanite Tailings by Carbothermal Reduction Nitridation

Synthesis of Rod-Like Α-Sialon by Carbothermal Reduction-Nitridation

Preparation of Sialon/Si<sub>3</sub>N<sub>4</sub>-SiC Composite Refractories Using Kyanite Tailings

Preparation of Sialon/Si3N4-SiC Composite Refractories Using Kyanite Tailings

Fabrication and properties of Al 2O 3-SiC/Sialon composite refractories

Fabrication and Properties of Al<sub>2</sub>O<sub>3</sub>-SiC/Sialon Composite Refractories

Preparation and Characterization of Β-Sialon Ceramics from High Aluminium Fly Ash Via Carbothermal Reduction-Nitridation

Synthesis of α-Sialon by High Temperature Nitridation Reaction

Synthesis of Sialon Powders from Aluminium Dross and Fly Ashes

Preparation Of Al2o3-Sic Composite Powder From Kyanite Tailings Via Carbothermal Reduction Process

Synthesis of Sialon-Ti(N,C) Composites Via Carbothermal Reduction-Nitridation from Pyrophyllite and Rutile

Influence of Process Parameters on Synthesis of Si3N4 Powders from Iron Ore Tailings

Synthesis of Β-Sialon/ti(c,n) Composites Using Low and Middle Grade Bauxite and Ilmenite by Carbothermal Reduction-Nitridation

Phase transformation of high aluminium fly ash in carbothermal reduction–nitridation at high temperatures

Synthesis of alpha-Sialon by High Temperature Nitridation Reaction

Synthesis of Si 3 N 4 powder with tunable α/β-Si 3 N 4 content from waste silica fume using carbothermal reduction nitridation

Synthesis of Sialon-Mullite Composites Using Fly Ash by Carbon-Thermal Reduction Nitridation

Study on Synthesizing Diphase Sialon from Lower Al2O3 Bauxite by Carbothermal Reduction-Nitridation

Synthesis of Fe<sub>3</sub>Si-Ti(C<sub>0.3</sub>, N<sub>0.7</sub>) Multiphase Composite Ceramic from Iron Tailings and its Properties