Abstract:Herein, Si3N4 powders of comparatively high α‐phase but with distinct morphologies, especially α‐Si3N4 fibers, were successfully prepared by a developed combustion synthesis (CS) strategy. Different proportions of Fe and Fe2O3 were innovatively doped in reactants as additives to control the phase constitution and their relative percentage, as well as morphologies of final microstructures. One step further, the effects of Fe‐contained impurities on the CS process were rationally proposed and verified based on a series of meticulous designed experiments. It turns out that two contradictory effects of metal Fe on the formation of α‐Si3N4 synergistically play vital roles in the CS reaction. The existence of metal Fe can accelerate the crystallization of the amorphous SiO2, which act as protection layer outside the Si powders and subsequently promote the generation of gaseous SiO. These gaseous SiO easily reacts with N2 and eventually form α‐Si3N4. On the other hand, the formation of β‐Si3N4 will be promoted by the assistance of some liquid phases, and in this case, they mainly come from the reaction between Fe and Si. For this study, when the content of doped Fe is below 2 mol%, the prior effect on promoting α‐phase content is pronounced. Otherwise, the latter dominates the CS process as the content of Fe additive is further increased above 2 mol%. In a different way, Fe2O3 mainly encourages the formation of β phase through the large amount of newly generated liquid phases, although the reduced SiO2 and Fe may still promote the α/β ratio on some extent.

Influence of Process Parameters on Synthesis of Si3N4 Powders from Iron Ore Tailings

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

Synthesis of Environment-Friendly Sialon/SiC Multiphase Ceramics from Cheap Nonmetallic Resources

Synthesis of monodisperse and high-purity α-Si3N4 powder by carbothermal reduction and nitridation

Synthesis of Si 3 N 4 powder with tunable α/β-Si 3 N 4 content from waste silica fume using carbothermal reduction nitridation

Synthesis of β-Si3N4 powder from quartz via carbothermal reduction nitridation

Preparation of Si 2 N 2 O from Flashing Combustion Synthesized Si 3 N 4 and Silica Fume

Synthesis of Spherical Si3N4 Powders by Liquid‐phase Modified Carbothermal Reduction and Nitridation

Influence of Temperature on Phase Composition of Nitridation Products from Ferrosilicon Alloy

Synthesis of Fe<sub>3</sub>Si-Ti(C<sub>0.3</sub>, N<sub>0.7</sub>) Multiphase Composite Ceramic from Iron Tailings and its Properties

Studies of synthesizing the SiC nanometer powders by chemical vapor reaction

Influence of Temperature on Phase Composition of Nitridation Products from Rutile and Fly Ash

Effect of Fe‐Contained Species on the Preparation of Α‐si3n4 Fibers in Combustion Synthesis

Effect of Reaction Temperature on the Synthesis of Β-Sialon/ti(c, N) Composites from Low Grade Bauxite and Ilmenite

Synthesis of TiN-Si3N4 Composites from Rutile and Quartz by Carbothermal Reduction Nitridation

Preparation and Effectiveness of Slow‐release Silicon Fertilizer by Sintering with Iron Ore Tailings

Fabrication of Electroconductive Si3N4–TiN Ceramic from Iron Ore Tailing

Effect of Impurities MgO, CaO, Al2O3, AlN and Al on Α/β Ratio in Combustion Synthesis of Α-Si3n4

Effect of Ti-Si-Fe alloy on the nitriding behavior of Si powder

Thermodynamical Analyses for the Preparation of Si3N4 Powder

Influences of Carbon Contents on the Products of Carbothermal Reduction-nitriding of Natural Quartz