Synthesis of β-Si3N4 powder from quartz via carbothermal reduction nitridation

Kai Chen,Zhaohui Huang,Yangai Liu,Minghao Fang,Juntong Huang,Youguo Xu

DOI: https://doi.org/10.1016/j.powtec.2012.11.036

IF: 5.64

2013-01-01

Powder Technology

Abstract:β-Si3N4 powder was synthesized via carbothermal reduction nitridation (CRN) method using quartz as starting material. The influence of synthesis temperature, C/SiO2 molar ratio and amount of Fe2O3 additive on the phase transformation and micro-morphology of β-Si3N4 powder was investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and high-resolution transmission electron microscopy (HRTEM). The results showed that the optimal experimental conditions for the CRN synthesis of β-Si3N4 powder were 3h sintering at 1600°C in flowing nitrogen atmosphere with C/SiO2 molar ratio of 2.0 and amount of Fe2O3 additive of 5.0wt.%. The prepared β-Si3N4 grains present a short hexagonal, rod-like morphology. Changes in experimental parameters affect the phase compositions and the morphology of the product. Excessive carbon promoted the formation reaction of β-SiC. Fe2O3 additive exerted a significant promotion on the formation of β-Si3N4 in CRN process by forming the low melting point eutectics.