Abstract:The non-oxide-reinforced phase AlN-SiC solid solution with high performance was successfully synthesized in the resin-bonded Al-Si-SiC composites under flowing nitrogen at 1300 °C. The AlN-SiC solid solution was synthesized by three paths of liquid-solid, gas-solid and gas-gas reactions through modulation of Al/Si ratio, and controllable microstructure of AlN-SiC solid solution was attained. The phase composition and microstructure of the sintered samples were characterized by XRD and SEM, combined with thermodynamics, the formation mechanism of AlN-SiC solid solution was investigated and the reaction model was established. Al was not detected while Si was detested by XRD. Granular, short columnar and whisker-like AlN-SiC solid solution were generated and their positions varied. As the temperature increases, the partial pressure of oxygen decreases due to the oxidation of Al, Si and SiC on the surface of the sample, inside the sample, the active oxidation takes place, generating Al2O(g), SiO(g) and CO(g). Due to the low oxygen partial pressure, Al is preferentially nitrided to form a thin AlN layer on its surface. The AlN layer is broken as the temperature increases, then liquid Al with carbon from resin begins to flow, leaving the residual shell of AlN in situ. When it flows to the surface of Si, Al-Sialloy is formed locally inside the Si particles under the wetting effect of C, then hexagonal AlN-SiC solid solution is formed inside the Si shell. Part of SiO(g) + CO(g) diffuses into the interior of the AlN residual shell and reacts by aggregation to form a granular AlN-SiC solid solution in the shell wall; others diffuses into the pores of the sample for vapor deposition, and finally forms stacked hexagonal flaky whiskers. The in-situ generated of AlN-SiC solid solution with multiple morphologies in the composite plays a joint toughening effect, which can significantly enhance the comprehensive performance of the composite. In this experiment, the synthesis of AlN-SiC solid solution without sintering aids under normal pressure at a low temperature. It is expected to be applied to the blast furnace and to realize the longevity of blast furnace.

Preparation of Si 2 N 2 O from Flashing Combustion Synthesized Si 3 N 4 and Silica Fume

Combustion Synthesis of MgSiN2 Powders and Si3N4‐MgSiN2 Composite Powders: Effects of Processing Parameters

Combustion synthesis of α-Si3N4 powders using in-situ nano-SiO2 coated Si and Si3N4 reactants

Preheating-assisted Combustion Synthesis of Β-Si3n4 Powders at Low N2 Pressure

Microstructure and Thermo‐Kinetics Analysis in Combustion Synthesis of Si3N4 with High α‐Phase Content

On the Progress of Combustion Synthesis of Si<sub>3</sub>N<sub>4</sub> Ceramic: From Laboratory Research to Industrial Production

Reaction Mechanisms of Combustion Synthesis of Si<sub>3</sub>N<sub>4</sub> -Sic -Tin Ceramics

Additive‐Assisted Nitridation to Synthesize Si3N4 Nanomaterials at a Low Temperature

Synthesis of Silicon Carbide Nanopowder Using Silica Fume

Effects of temperature, atmosphere, silicon occurrences on fine particle formation from vaporization during high-silicon coal combustion

Reaction mechanisms of combustion synthesis of Si3N4 -SiC -TiN ceramics

Formation mechanism of AlN-SiC solid solution with multiple morphologies in Al-Si-SiC composites under flowing nitrogen at 1300 °C

On the Progress of Combustion Synthesis of Si3n4 Ceramic: from Laboratory Research to Industrial Production

Effect of Fe‐Contained Species on the Preparation of Α‐si3n4 Fibers in Combustion Synthesis

Combustion synthesis of Si2N2O powder for photovoltaic silicon casting application

A simple method to synthesize Si3N4 and SiO2 nanowires from Si or Si/SiO2 mixture

The Role of MgSiN2 During the Sintering Process of Silicon Nitride Ceramic

Synthesis mechanism of AlN–SiC solid solution reinforced Al2O3 composite by two-step nitriding of Al–Si3N4–Al2O3 compact at 1500 °C

Synthesis mechanism of α-Si3N4 whiskers via SiO vapor in reaction bonded Si3N4-SiC composite

MICROSTRUCTURE OF Si3N4-TiN-SiC CERAMICS DURING COMBUSTION SYNTHESIS PROCESS

Combustion synthesis Si3N4 powders by using activation process