Abstract:The Gibbs free values of different SiAlON were assessed by the thermodynamic quasi-paraboloid rule in Si3N4-AlN-SiO2-Al2O3 system and the thermodynamic parameter for beta-SiAlON were explored at 1800K. The synthesis of beta-SiAlON based oil coal gangue and carbon black by carbonthermal reduction nitridation method, and phase transformation of beta-SiAlON powder ill various atmospheres (such as air or nitrogen of different Purity) were discussed in detail. Thermodynamic analysis reveals that different SiAlON can be synthesized ill Suitable atmosphere parameter Y(Y = Ig (P-O2/P-theta) - 2/3Ig (P-N2/P-theta)) at 1800K, and low Y value is beneficial to synthesis of beta-SiAlON. When excessive carbon exists in the atmosphere, with the increase of purity (alpha) of initial nitrogen, the Y Value decreases, and the relationship between purity(alpha) and Y value Is Y = 2lg[ (2 - 2 alpha)/(2 - alpha)] - 2/3lg[alpha/(2 - alpha)] - 15.616. The experiment results shows that the suitable initial parameters based on thermodynamic analysis is highly advantageous in controllable synthesis of high-purity beta-SiAlON, the proper initial parameters is that samples, burying in coke, are sintered at 1800K in a flowing nitrogen atmosphere, the purity range of nitrogen is about 0.995-0.999.

The Preparation of Β-Sialon Powder from High-Alumina Fly Ash: an Experimental Study

A Study on the Preparation of the Sialon Powder with Fly Ash by the Silicon Thermal Reduetion-nitridation Method

Synthesis of Sialon Powders from Aluminium Dross and Fly Ashes

Preparation of Β-Sialon from Fly Ash by Carbothermal Reduction-Nitridation Reaction

Preparation of Sialon Using Fly Ash with High Content of Al<sub>2</sub>O<sub>3</sub>

Preparation of Sialon Using Fly Ash with High Content of Al2O3

Preparation of Fly Ash-Based Porous Ceramic with Alumina as the Pore-Forming Agent

Preparation and Characterization of Β-Sialon Ceramics from High Aluminium Fly Ash Via Carbothermal Reduction-Nitridation

Phases transformation of high-alumina fly ash under carbothermal reduction and nitridation

Synthesis of Sialon-Mullite Composites Using Fly Ash by Carbon-Thermal Reduction Nitridation

Nano Β-Sialon Powder Synthesized by Carbothermal Reduction and Nitridation of Ultrafine Al2O3-SiO2 Mixture Employing Sol-Gel Techniques

Preparation of β-Sialon /SiC composite powder by carbothermal reaction of coal-mine schist

Synthesis of Fe-Sialon Composites Using High Alumina Coal Gangue by Carbothermal Nitridation

Study on Synthesizing Diphase Sialon from Lower Al2O3 Bauxite by Carbothermal Reduction-Nitridation

Sintering and Composition of a Powder Mixture of Fine Al2O3 and Beta-Sialon Composite Made from Bauxite

Preparation of Ca-α/β-sialon powders by microwave reaction nitridation

The Carbon Environment Effects on Phase Composition and Photoluminescence Properties of Β-Sialon Multiphase Materials Prepared from Fly Ash Acid Slag

Dilithium Dialuminium Trisilicate Crystalline Phase Prepared from Coal Fly Ash

Phase transformation of high aluminium fly ash in carbothermal reduction–nitridation at high temperatures

Preparation of beta sialon/SiC composite powder by carbothermal reaction of coal mine schist

Controllable Synthesis Of High-Purity Beta-Sialon Powder