A Study on the Preparation of the Sialon Powder with Fly Ash by the Silicon Thermal Reduetion-nitridation Method

CAO-Ying,LI Wei-dong,LI Jin-hong

DOI: https://doi.org/10.3969/j.issn.1007-2802.2006.04.014

2006-01-01

Abstract:The Sialon powder was prepared with the raw products,which is made with fly ash and silicon powder in the flowing N_2 gas,by using the silicon thermal reduction nitridation method.The Sialon mass content variation,phase transformation regularity and the morphological features of the raw products,which were nitrided at temperatures from 1350℃ to 1500℃ for 6 hours,have been investigated by utilizing XRD and SEM.The results indicated that the Sialon mass contents of the products formed at 1350℃,1400℃ and 1450℃ respectively are gradually increased.Whereas the Sialon mass content of the product formed at 1500℃ is much lower than those of the products formed at 1350℃,1400℃ and 1450℃.The β-Sialon content of the product formed at 1450℃ is the highest while its O'-Sialon content is the lowest.In addition,the total Sialon solid solution content of 85.6% in the product formed at 1450℃ can be achieved by adding silicon beyond theoretical content of 10% into fly ash.The Sialon occurs mainly as petal aggregates,surrounding with a few white Si_3N_4 fibers.