Abstract:We fabricated spin-valve devices made of organic semiconductor thin films sandwiched between ferromagnetic half-metal La2/3Sr1/3MnO3 (LSMO) and cobalt electrodes, using three different organic molecules. Subsequently, we studied the spin injection and transport properties by measuring the device magnetoresistance (MR) response at various biasing voltages V and temperatures T. We found that the spin-valve MR response in all devices monotonically decreases with V and is asymmetric with respect to the voltage polarity. We also found a steep MR decrease with T, where it vanishes at T similar to 220 K, similar to other MR responses in inorganic tunneling junction devices based on LSMO and Co ferromagnetic electrodes. In contrast, the 1/2 photoluminescence detected magnetic resonance of the organic interlayer, which directly depends on the spin-lattice relaxation rate of polarons in the organic semiconductor, was found to be temperature independent. We thus conclude that the steep MR dependence on T is due to the temperature dependence of the interfacial spin polarization of the LSMO electrode, which also drastically decreases up to T similar to 220 K. We thus conclude that (i) the spin-lattice relaxation time in organic semiconductors should not be the limiting factor in fabricating room temperature organic spin valves, and (ii) in order to achieve room temperature spin-valve operation with substantial MR value, spin-injection electrodes other than LSMO need to be involved, having large and less temperature dependent spin polarization.

Reduction of hysteresis for spin valve film by annealing method

Valve Behavior Of Giant Magnetoimpedance In Field-Annealed Co70fe5si15nb2.2cu0.8b7 Amorphous Ribbon

Effect of Annealing on SAF Spin Valves with Variable Easy Axis of Free Layer

Fabrication of GMR Linear Sensor Based on Spin Valve

Spin Response in Organic Spin Valves Based on La2/3sr1/3mno3 Electrodes

Organic spintronics: The case of Fe/Alq3/Co spin-valve devices

Effect of Tension Annealing on Giant Magneto-Impedance in Glass-Covered Co-rich Amorphous Wire

Improvement of Magnetoresistive Character of NiO/NiFeCo/Cu/NiFeCo Exchange-Biased Spin-Valves Through Annealing in Magnetic Field

Annealing Effect on Magnetoresistance in Nio-Co-Cu Based Spin Valves

High Giant Magnetoresistance and Thermal Annealing Effects in Perpendicular Magnetic [Co/ni]n-Based Spin Valves

Study on the Structure of Spin Valve for GMR Sensor with Low Coercivity

Investigation on the Performance of Spin Valve Magnetic Sensor with Thermal Stability

Influence of reactive ion etching process on magnetic properties of giant magnetoresistive spin valve

Dependence of GMR on NiFe Layer Thickness in High Sensitive Simple Spin Valve

Giant Magnetoresistance Enhancement In Spin Valves With Nano-Oxide Layers

Study on GMR Magnetic Sensor with Low Coercivity and the Single Domain Model

Structure Optimization and Thermal Annealing Effect of IrMn-based Bottom Spin Valves

High-sensitivity GMR with low coercivity in top-IrMn spin-valves

Modeling and Analysis of Nano-Sized GMRs Based on Co,NiFe and Ni Materials

Study on influence factors of GMR effect in NiO/NiFeCo/Cu/NiFeCo spin-valves

Optimization of Ta Buffer Layer in IrMn Top Spinvalve