Abstract:For bottom spin-valves of $\mathrm{NiO}∕\mathrm{Fe}∕\mathrm{Cu}∕{\mathrm{Gd}}_{1\ensuremath{-}x}{\mathrm{Co}}_{x}$, giant magnetoresistance has been measured as a function of thickness and composition of $\mathrm{GdCo}$ layers as well as temperature. For all spin-valves involved here, the giant magnetoresistance has been attributed to contributions of spin-dependent scattering at interfaces and in bulk. The interfacial contribution produces positive giant magnetoresistance ratio for various compositions of $\mathrm{GdCo}$ alloys. However, the bulk contribution produces negative one for the Co contents from $50\phantom{\rule{0.3em}{0ex}}\mathrm{at}.\phantom{\rule{0.2em}{0ex}}%$ to a critical value ${x}_{\mathrm{C}}(R)$ (between $69\phantom{\rule{0.3em}{0ex}}\mathrm{at}.\phantom{\rule{0.2em}{0ex}}%$ and $77\phantom{\rule{0.3em}{0ex}}\mathrm{at}.\phantom{\rule{0.2em}{0ex}}%$) and positive one for higher Co contents. It is suggested that the interfacial asymmetric factor of spin-dependent scattering is larger than 1.0 at the $\mathrm{Cu}∕\mathrm{GdCo}$ for various alloy compositions of $\mathrm{GdCo}$ and that the bulk asymmetric factor in $\mathrm{GdCo}$ layer is smaller and larger than 1.0 for Co contents below and above ${x}_{\mathrm{C}}(R)$, respectively. For spin valves with Co contents below and/or above ${x}_{\mathrm{C}}(R)$, the giant magnetoresistance ratio varies nonmonotonically and/or monotonically as a function of the $\mathrm{GdCo}$ layer thickness (temperature) for a specific temperature (a specific $\mathrm{GdCo}$ layer thickness), respectively. The change of the bulk asymmetric factor in the $\mathrm{GdCo}$ layer with the alloy composition can be attributed to the variation of either the spin alignment of Co and Gd atoms or the spin polarization of the $\mathrm{GdCo}$ layer.

High Giant Magnetoresistance and Thermal Annealing Effects in Perpendicular Magnetic [Co/ni]n-Based Spin Valves

Valve Behavior Of Giant Magnetoimpedance In Field-Annealed Co70fe5si15nb2.2cu0.8b7 Amorphous Ribbon

Organic spintronics: The case of Fe/Alq3/Co spin-valve devices

Magneto-Transport Studies of Fe/Alq(3)/Co Organic Spin-Valves

Role of Tbfe on Perpendicular Magnetic Anisotropy and Giant Magnetoresistance Effect in [Co/ni](n)-Based Spin Valves

Investigation on the Performance of Spin Valve Magnetic Sensor with Thermal Stability

Improvement of Magnetoresistive Character of NiO/NiFeCo/Cu/NiFeCo Exchange-Biased Spin-Valves Through Annealing in Magnetic Field

Study on influence factors of GMR effect in NiO/NiFeCo/Cu/NiFeCo spin-valves

Giant Magnetoresistance Enhancement In Spin Valves With Nano-Oxide Layers

Hysteretic Giant Magnetoresistance Curves Induced by Interlayer Magnetostatic Coupling in [pd/co]/cu/co/cu/[co/pd] Dual Spin Valves

Inverse Giant Magnetoresistance Infe∕cu∕gd1−xcoxspin-Valves

Dependence of GMR on NiFe Layer Thickness in High Sensitive Simple Spin Valve

Magnetoresistive Behavior and Magnetization Reversal of NiFe/Cu/CoFe/IrMn Spin Valve GMRs in Nanoscale

Piezoelectric Enhancement of Giant Magnetoresistance in Spin-Valves with Different Magnetic Anisotropies

Study on GMR Magnetic Sensor with Low Coercivity and the Single Domain Model

Effect of Thermal Stability on Magnetoresistance in NiO Spin Valve

Pinning effect and thermal stability study in L1 FePt-pinned spin valves

Micromagnetic Studies of Antiferromagnetism and Resistance-Field Curves in Giant Magnetoresistive Co/Al/Nife

High-sensitivity GMR with low coercivity in top-IrMn spin-valves

[Co/ni] N -Based Synthetic Antiferromagnet with Perpendicular Anisotropy and Its Application in Pseudo Spin Valves

Annealing Effect on Magnetoresistance in Nio-Co-Cu Based Spin Valves