Abstract:Abstract Several coal-fired thermal power boilers with the same sub-critical parameters in Mengxi area of Inner Mongolia have successively suffered from cracking and leakage failure events of reheater connecting pipes, most of which occur at chamfered back tool grooves on the inner wall grooves of pipe welding joints. In order to find out the cause of cracking, typical failure samples were intercepted for macro-morphology, microscopy, SEM, chemical composition, mechanical properties, wall thickness measurement analysis and design and operation data investigation of several boiler equipment. The results show that comprehensive factors such as deviation of burning coal type from design of boiler, automatic dispatching of AGC load in power grid, low nitrogen combustion modification and so on cause changes in boiler combustion conditions and operation, which results in excessive high input level of reheater cooling water, resulting in long-term alternating thermal stress and non-periodic vibration of straight pipe and elbow arranged after fine-tuning of refrigerant flow direction in reheater. Finally, thermal fatigue cracks are induced to initiate and propagate through the stress concentration area of the chamfered knife groove of the inner wall of pipe welded joints.

Analysis on a Burst High-Temperature-Reheater Pipe in a Power Plant

BURST ANALYSIS OF HIGH TEMPERATURE RE-HEATER PIPE OF POWERSTATION

Corrosion Failures of High Temperature Heat Pipes

Cause Analyses of the Weld Seam Cracks of a Prehydrogenating Reactor

Cracking Analysis on Water Cooling Wall Pipe in Power Plant

Failure Analysis of Bursting on the Inner Pipe of A Jacketed Pipe in A Tubular Heat Exchanger

Analysis of Invalidation Mechanism of Reheater of 1100t/h Boiler

Analysis of Frequent Tube Burst of High Temperature Reheater in 600 MW Unit

Failure Analysis on Bursted High Temperature Steam Pipe of Heavy Oil Well

Failure Analysis on Water Wall Tube Burst of Heating Furnace

FRACTURE ANALYSIS OF THE PIPES FOR EXCHANGING BOILER'S SURPLUS HEAT

Burst Cause Analysis for the Reheater Tube of the 2×300MW Unit Boiler in Huaneng Shantou Power Plant

Failure Analysis on Abnormal Bursting of Heat Transfer Tubes in Spiral-Wound Heat Exchanger for Nuclear Power Plant

FAILURE ANALYSIS OF BOILER TUBE

State analysis on reactor furnace pipe used over a design cycle

Cause Analysis of Tube Burst of the Condenser in a Power Plant

Failure Analysis of HP Steel Tube Rupture of Hydrogen Reformer in a Refinery

Analysis on the cause of crack in connection pipeline of subcritical boiler reheater

Analysis and Research on Crack Failure of P91 Pipe

Burst failure analysis on 20G steel low temperature superheater tube of biomass-fired boiler

Experimental and simulative failure analysis of reformer furnace outlet manifolds serviced in aromatic plant