Analysis on the cause of crack in connection pipeline of subcritical boiler reheater

Yanfei Zhang,Feng Yun,Wenxuan Fang,Haixue Wang

DOI: https://doi.org/10.1088/1755-1315/508/1/012202

2020-05-01

IOP Conference Series: Earth and Environmental Science

Abstract:Abstract Several coal-fired thermal power boilers with the same sub-critical parameters in Mengxi area of Inner Mongolia have successively suffered from cracking and leakage failure events of reheater connecting pipes, most of which occur at chamfered back tool grooves on the inner wall grooves of pipe welding joints. In order to find out the cause of cracking, typical failure samples were intercepted for macro-morphology, microscopy, SEM, chemical composition, mechanical properties, wall thickness measurement analysis and design and operation data investigation of several boiler equipment. The results show that comprehensive factors such as deviation of burning coal type from design of boiler, automatic dispatching of AGC load in power grid, low nitrogen combustion modification and so on cause changes in boiler combustion conditions and operation, which results in excessive high input level of reheater cooling water, resulting in long-term alternating thermal stress and non-periodic vibration of straight pipe and elbow arranged after fine-tuning of refrigerant flow direction in reheater. Finally, thermal fatigue cracks are induced to initiate and propagate through the stress concentration area of the chamfered knife groove of the inner wall of pipe welded joints.