Abstract:The stability of W–Cu functionally graded material (FGM) as a heat sink connecting material is of significant importance for long-term service under high-temperature thermal cycling conditions. In this study, W–Cu FGM was successfully fabricated by powder metallurgy method. Various thermal shock experiments were performed on the samples at different temperatures and cycles, and a comprehensive investigation was conducted into its service failure mechanisms. The findings demonstrate that as the temperature increases to 1000 °C, the layer with low copper content gradually developed microcracks, and the microstructure changed from the original uniform distribution to a copper granular exudation, ultimately forming a network-like copper layer. The layer with high copper content undergoes a transition from slight undulations and roughness to the emergence of numerous cracks and pores, accompanied by the formation of a larger area of copper pool structures. After 1000 °C thermal shock for 200 cycles, the thermal conductivity decreases from 215.33 W m −1 K −1 to 168.24 W m −1 K −1 , the bending strength decreased from 686.75 MPa to 115.77 MPa at room temperature, with reductions of 22.4 % and 81.2 %, respectively. At this point, the sample severely failed. The study highlights that the thermal shock failure mechanism of the gradient W–Cu samples is a novel multifactor coupled failure mechanism. It is influenced by the combined effects of crack initiation and propagation induced by thermal stress and the evolution of microstructural changes.

Fabrication of W/Cu functionally graded material and analysis of thermal cycle stress

Fabrication and microstructure of W/Cu functionally graded material

HIGH HEAT LOAD PROPERTIES OF W/Cu FUNCTIONALLY GRADED MATERIALS

Fabrication of W–Cu Functionally Graded Material with Improved Mechanical Strength

Fast fabrication of W-Cu functionally graded material by high-gravity combustion synthesis and melt-infiltration

Fabrication of W/Cu Graded Heat-sink Materials by Electroless Plating and Powder Metallurgy

Tungsten Joining with Copper Alloy and Its High Heat Load Performance

Multi-factor coupled failure mechanism of W–Cu functionally graded material under thermal shock service

Functionally Graded W-Cu Materials Prepared from Cu-Coated W Powders by Microwave Sintering

Effect of the Iter Fw Manufacturing Process on the Microstructure and Properties of A Cucrzr Alloy

Investigation for the Fracture Process of WCp/Cu Functionally Graded Materials under Three-Point-Bending

Thermal shock behavior of W/Cu functionally gradient material

Fabrication and properties of W-Cu functionally graded materials by tape calendaring method

Optimum design of W/Cu functionally graded material for thermal stress mitigation

Microstructure and Properties of Wcp/Cu Layered Functionally Graded Materials Prepared by Vacuum Hot-Pressed Sintering

Design and Thermal Shock Performance of W/Cu Functionally Graded Material used as Plasma Facing Component

Thermal stress simulation in TiB2-Cu functionally graded materials

Current Status of Design and Manufacture on W/Cu Interface of the Fist Wall Material

Characterization and stress relaxation of the functionally graded WC-Co/Ni component/stainless steel joint

Microstructural evolution of graded W-Cu materials under repeated thermal shocks

Fabrication Of Sic/Cu Functionally Gradient Material By Graded Sintering