Abstract:Herein, high-density W-Cu functionally graded materials were successfully prepared by explosive compaction-welding sintering. The minimum detonation pressure required for the explosive compaction-welding and minimum pressure needed for the powder consolidation were calculated. A method for calculating the equation of state of the porous materials was presented, and the data of the porous W-Cu composites thus obtained were used in the numerical simulation. The pressure changes in the powder layers during the explosive compaction-welding was numerically simulated, which showed that the parameters of the explosive used in the experiment were sufficient for densifying the powders. The scanning electron microscope test results exhibited that the layers of the graded materials were tightly integrated. The interface between the W-Cu particles was enriched with Cu, whereas there was no growth of the tungsten particles in the W-50 wt.% Cu layer. Tungsten and copper enrichment occurred in some regions in the W-70 wt.% Cu layer, whereas there was a growth of tungsten particles in some areas in the W-30% wt. Cu layer, the reasons for which were analyzed. The overall porosity of the three powdered layers in the five-layer gradient material was 0.36%. The contents of tungsten and copper showed a gradient trend similar to the added W-Cu composite powders. The Vickers hardness test results also exhibited a gradient trend. The shear strength between the layers was measured. The shear fractures were analyzed.

Fabrication and properties of W-Cu functionally graded materials by tape calendaring method

Fabrication of W-Cu functionally graded material by spark plasma sintering method

Functionally Graded W-Cu Materials Prepared from Cu-Coated W Powders by Microwave Sintering

Fabrication of W/Cu functionally graded material and analysis of thermal cycle stress

Fabrication of W–Cu Functionally Graded Material with Improved Mechanical Strength

Experimental and Numerical Studies on W–Cu Functionally Graded Materials Produced by Explosive Compaction–welding Sintering

Fabrication and microstructure of W/Cu functionally graded material

Microstructure and Properties of Wcp/Cu Layered Functionally Graded Materials Prepared by Vacuum Hot-Pressed Sintering

Fabrication and Application of W/Cu Functionally Graded Material

Fabrication of W/Cu Graded Heat-sink Materials by Electroless Plating and Powder Metallurgy

Fast fabrication of W-Cu functionally graded material by high-gravity combustion synthesis and melt-infiltration

W–Cu Composite with High W Content Prepared by Grading Rounded W Powder with Narrow Particle Size Distribution

A Novel Approach for Fabrication of Functionally Graded W/Cu Composites Via Microwave Processing

Investigation for the Fracture Process of WCp/Cu Functionally Graded Materials under Three-Point-Bending

Fabrication and properties of Al/Al-Cu functionally graded material

Microstructure and Properties of W Cu Composites with Low Copper Content at Different Sintering Temperatures

Structure and Property of W-Ni-Cu Functionally Graded Materials by Composite Electrodeposition

Preparation and Properties of W-15Cu Composite by Electroless Plating and Powder Metallurgy

Effect of Tape Casting Procedure on Structure and Microwave Characteristics of Tapes

Process of Manufacturing Fine-Grained W-Cu Composite Material

WCu20 alloy thin sheet prepared by tape-casting and infiltration sintering