Abstract:Heterogeneous W-steel joining components will produce brittle intermetallic compounds (IMCs) and significant residual stress in the interface. Adding a Cu interlayer serves as an effective solution. Nevertheless, the strengthening of W-Cu-steel joints is restricted because W-Cu and Cu-steel are members of binary immiscible and finite solid solution systems. Thus, accomplishing interface alloying by overcoming the positive generating energy of insoluble systems and opening up interatomic diffusion channels is a crucial issue to be addressed. In this work, casting and brazing technologies were incorporated into bonding W-Cu-steel to provide a high temperature field, as well as the dissolving and wetting of Cu-based liquid phase to refractory W. It is shown that the superior tensile strength of the W/Cu castings-steel brazed joints (similar to 264 MPa) was achieved, and the joint survived 1000 cycles of thermal fatigue under 1 MW/m(2). To assess the effects of brazing and casting on the W-Cu-steel joint, a detailed analysis was conducted on the mechanism of atomic diffusion in the joint interface. It is considered that in W-Cu joining, casting provided a higher thermodynamic driving force than brazing, thus achieving better interatomic diffusion and a wider microalloying region. Cu-steel joining achieved good alloying and forming dendritic extensions by intergranular diffusion. Based on the process optimization results, the feasibility of preparing the U-shaped first wall (FW) mock-up with W armor using brazing technology was verified. This study provides a new technological path, offering a major design and manufacturing guide for plasma facing components (PFCs).

Characterization and stress relaxation of the functionally graded WC-Co/Ni component/stainless steel joint

Interfacial microstructure and mechanical properties of WC–Co/40Cr joints brazed at low–temperature with Ag–Cu–Ti + Sn novel filler

Characterization and forming process of a functionally graded WC-Co/Ni composite

Investigating the effect of WC reinforcements in Cu Ti composite filler on the microstructural evolution and mechanical characteristics in brazing C f /SiC and GH3536

Microstructure and Properties of WC–Co/3Cr13 Joints Brazed Using Ni Electroplated Interlayer

Investigating the Effect of WC Reinforcements in Cu Ti Composite Filler on the Microstructural Evolution and Mechanical Characteristics in Brazing Cf/SiC and GH3536

Fabrication and Micro-Structure of a Multilayer Functionally Graded (wc–co)–ni Composite

Microstructure Transformation and Crack Sensitivity of WC-Co/steel Joint Welded by Electron Beam

Research on Residual Stress in Copper/Al2O3 Ceramic/Stainless Steel Composite Structure Brazed Joint

Interfacial Strengthening Mechanism of C/C/Nb0.74CoCrFeNi2/Nb Brazed Joints: Stress-relieving Effects of the FCC Phase

Improving the Interface Strength and Fatigue Property of W-Cu-steel Brazed Joint Via Induced Interface Alloying

Graded composition and structure in nanocrystalline Ni–Co alloys for decreasing internal stress and improving tribological properties

The dependence of microstructure and mechanical properties on substrate heat treatment in AlN ceramics/AgCuTi/316 stainless steel brazed joints

Effect of bonding process on the microstructures and strength of W/steel joints with a W-Cu-Ni interlayer

Brazing of C/C composites and 304 stainless steels via Ni/Mo composite interlayer

Tungsten/steel diffusion bonding using Cu/W–Ni/Ni multi-interlayer

Relation of Internal Stress and Fracture Behavior of Symmetrically Graded Al2O3/TiC/Ni

Brazing ZrO2 Ceramic and TC4 Alloy by Novel WB Reinforced Ag-Cu Composite Filler: Microstructure and Properties

Interfacial microstructure and strengthening mechanism of W/steel diffusion bonding joint using a porous NiFeWss interlayer prepared by in-situ reduction

Interfacial microstructure and mechanical properties of joints between ZrO 2 ceramic and 316 stainless steel brazed using Ag–Cu–In–Ti filler

Investigation on Microstructure of Electron Beam Welded WC-Co/40Cr Joints