Intergranular precipitation behavior and its influence on the stress relaxation cracking susceptibility of Super304H austenitic stainless steel weld metal during long-term aging

Xiaopeng Xiao,Dianzhong Li,Yiyi Li,Shanping Lu
DOI: https://doi.org/10.1016/j.matchar.2021.111309
IF: 4.537
2021-08-01
Materials Characterization
Abstract:<p>Stress relaxation cracking failure is widely reported in the materials used for thermal power plants, which seriously affected the safety of thermal power units under long-term service. In our study, the influence of intergranular precipitation behavior on the stress relaxation cracking susceptibility of Super304H austenitic stainless steel weld metal was investigated based on the pre-compressed CT technique. The 45° misorientation grain boundary has the lowest critical interfacial nucleation energy, followed by the grain boundaries away from the 45° misorientation. As a result, the coarse intergranular M<sub>23</sub>C<sub>6</sub> carbides were more prone to precipitate at 45° misorientation grain boundary, which led to the lowest resistance to stress relaxation cracking susceptibility at 35 to 45° grain boundary. Further analysis indicated that intergranular cavities were easily initiated at the non-coherent M<sub>23</sub>C<sub>6</sub>/γ interface. Since the non-coherent interface with a low Cr concentration zone and high specific interfacial energy had a lower strength, the lattice distortion at the non-coherent interface could lead to higher strain concentration.</p>
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing
What problem does this paper attempt to address?