Abstract:Background: Fe80B20 amorphous alloys exhibit excellent soft magnetic properties, high abrasive resistance and outstanding corrosion resistance. In this work, Fe80B20 amorphous micro-fibers with HC of 3.33 Oe were firstly fabricated and the effects of annealing temperature on the structure and magnetic properties of the fibers were investigated. Methods: In this study, Fe80B20 amorphous fibers were prepared by the single roller melt-spinning method. The structures of as-spun and annealed fibers were investigated by X-ray diffractometer (XRD) (PANalytical X,Pert Power) using Cu Kα radiation. The morphology of the fibers was observed by scanning electron microscopy (SEM) (HITACHI-S4800). Differential scanning calorimetry (DSC) measurements of the fibers were performed on Mettler Toledo TGA/DSC1 device under N2 protection. Vibrating sample magnetometer (VSM, Versalab) was used to examine the magnetic properties of the fibers. The resonance behavior of the fibers was characterized by an impedance analyzer (Agilent 4294A) with a home-made copper coil. Results: The X-ray diffusion (XRD) patterns show that the fibers remain amorphous structure until the annealing temperature reaches 500°C. The differential scanning calorimetry (DSC) results show that the crystallization temperature of the fibers is 449°C. The crystallization activation energy is calculated to be 221 kJ/mol using Kissinger formula. The scanning electron microscopy (SEM) images show that a few dendrites appear at the fiber surface after annealing. The result indicates that the coercivity HC (//) and HC (⊥) slightly increases with increasing annealing temperature until 400°C, and then dramatically increases with further increasing annealing temperature which is due to significant increase in magneto-crystalline anisotropy and magneto-elastic anisotropy. The Q value firstly increases slightly when the annealing temperature rises from room temperature (RT) to 300°C, then decreases until 400°C. Eventually, the value of Q increases to ~2000 at annealing temperature of 500°C. Conclusions: In this study, Fe80B20 amorphous fibers with the diameter of 60 μm were prepared by the single roller melt-spinning method and annealed at 200°C, 300°C, 400°C, and 500°C, respectively. XRD results indicate that the fiber structure remains amorphous when the annealing temperature is below 400°C. α-Fe phase and Fe3B phase appear when the annealing temperature rises to 500°C, which is above the crystallization temperature of 449°C. The recrystallization activation energy is calculated to be 221 kJ/mol. The coercivity increases with increasing annealing temperature, which attributes to the increase of total anisotropy. All the as-spun and annealed fibers exhibit good resonance behavior for magnetostrictive sensors.

Annealing Effects On Properties Of Bi-Substituted Garnet Films With Perpendicular Anisotropy Prepared By A Sol-Gel Method

Comparison on the crystallization characteristics of sol–gel derived (BiDy)3Fe5O12 garnet film and powder

Characterization of Bi-Substituted Dysprosium Iron Garnet Films Prepared by Sol-Gel Process

Effects of Annealing Temperature on the Structures, Ferroelectric and Magnetic Properties of Aurivillius Bi5ti3feo15 Polycrystalline Films

In Situ Optical Characterizations of the Annealing Effects Upon Sno2: F Films by Spectroscopic Ellipsometry

Structure and magneto-optical properties of fine-grain garnet thin film prepared by pyrolysis method

Effects of Post-Annealing Treatment on the Structural and Optical Properties of Cubic Mg Chi Zn1-Chi O Thin Films Grown on Sapphire

New Method to Improve the Structure and Magnetic-Optical Properties of Bismuth Garnet-Films

Effects of post-deposition annealing on the structure and magnetization of PLD grown Yttrium Iron Garnet films

Preparation of (BiAl)DyIG garnet magneto-optical recording films by sol-gel method

Effects of Crystal Structure, Morphology and Ion Diffusion During Annealing on Magnetic Properties of Hexagonal Barium Ferrite Films

The annealing effect on the magneto-optical properties of CoxAg100−x granular films

Annealing temperature effect on internal strain and ferroelectric properties of Bi3.25La0.75Ti3O12 thin films

Magnetic and Magneto-Optical Properties of Sputtered High Bi-substituted Al/BiGaDylG Double Layer Thin Films

Effect of annealing process on dielectric and multiferroic properties of Sol-Gel derived bismuth chromate thin films

Effects of annealing on the structure and magnetic properties of Fe80B20 magnetostrictive fibers

Long Time Annealing Effects on the Microstructures of the Sol–gelderived Nanocrystalline Thin Films of Rare Earthstabilized Zirconia

Effect of Annealing Temperature on Structural and Magnetic Properties of Co2TiO4 Ceramics Prepared by Sol-Gel Method

Magneto-optical Properties of Nanometer Crystal Giant Magneto-Optical BiAlDyIG Thin Film Materials Post-Treated by Rapid Recurrent Thermal Annealing Method

Effect of Annealing Temperature on the Properties of BaFe12O19 Thin Films Deposited on GGG (111) Substrates by Pulsed Laser Deposition

Investigation of the Effect of Annealing Temperature on Optical Properties of Lanthanum-Oxide Thin Films Prepared by Sol-Gel Method