Effect of Second Annealing on Magnetic Properties and Microstructure of (nddy)fecocub Magnets

W Wang,W Luo,YH Wen,LQ Yu,M Yan

DOI: https://doi.org/10.3321/j.issn:1002-185x.2005.10.030

2005-01-01

Abstract:The effect of a second annealing technique on the magnetic properties and microstructure of Nd12.0Dy2.8Fe74.7Co3.4Cu0.2B6.9 magnets have been investigated. The results show that the second annealing technique has little effect on residual magnetization and maximum energy product. Coercivity H-cj improves with the increase of annealing temperature, and the maximum can be achieved when annealed at 480 degrees C. Above 480 degrees C, H-cj decreases rapidly with the further increase of the second annealing temperature. When annealed at 480 degrees C, H-cj improves as increasing annealing time and the maximum H-cj can be achieved at 2h. Above 2h, the further increase of time has little effect on H-cj. SEM analysis shows that when annealed at 480 degrees C for 2h, the grain boundaries of the magnets are more smooth and the distribution of RE-rich phase in the grain boundaries is continuous and uniform.