Effects of Annealing at Ar Ambient on the Physical Properties of Zn0.66Co0.34O Thin Film

LIU Pu-cheng,QIU Dong-jiang

DOI: https://doi.org/10.3321/j.issn:1001-9731.2007.07.014

2007-01-01

Abstract:Zn0.66Co0.34O films were grown by reactive e-beam evaporation at 250℃ and then annealed in Ar ambient at 500℃ for 1h.Scanning electron microscope,X-ray diffraction(XRD) and vibrating sample magnetometer(VSM) were employed to characterize the microstructure and magnetic properties of Zn0.66Co0.34O film.XRD measurements revealed that both of as-grown and annealed Zn0.66Co0.34O films are homogeneous with a pure wurtzite structure.Room temperature M-H curves tested by VSM show that the as-grown film is superparamagnetic while the annealed film demonstrates a mixed magnetic characteristics of ferromagnetism and superparamagnetism.Such results suggest that by annealing treatment,some small crystal grains coalesced into relatively larger crystallites,whose sizes exceeded the superparamagnetic critical radius of Zn0.66Co0.34O material and correspondingly showed their ferromagnetic nature.However,probably duo to the fact that other grains still kept superparamagnetic,so the film emerged a mixed magnetic state of superparamagnetism and ferromagnetism.