Abstract:Nanocrystalline Ce-substituted yttrium iron garnet (YIG) powders of different compositions, Y3-x Ce x Fe5O12 (0 ≤ x ≤ 2.0), were synthesized by a combination of sol-gel auto-combustion and solid-state synthesis techniques. The as-obtained powder samples were sintered at 1150 °C for 10 h. The garnet structure formation is confirmed by the X-ray diffraction pattern, which shows that the calculated lattice parameter increased for x = 1.0 and shows a decreasing trend for x ≥ 1.0 with the addition of cerium ions. The lattice parameter increased from 12.38 Å to 12.41 Å for x ≤ 1.0 whereas it decreased from 12.412 Å to 12.405 Å with the cerium composition for x > 1.0. The average particle size determined by high resolution transmission electron microscopy is in the range of 50 to 90 nm and found to increase with the substitution of cerium ions in YIG. The room temperature magnetic parameters such as saturation magnetization, coercivity and remanence magnetization are greatly affected by the substitution of cerium ions. The values of saturation magnetization decrease from 25.5 to 15 emu g-1 whereas coercivity increases from 1 to 28 Oe with the substitution of cerium ions. The pure YIG sample shows polycrystalline nature that changed towards a single-crystal structure leading to a preferred-(100) orientation with the Ce substitution. The change from a ring to a spotty pattern observed in SAED confirmed the crystalline phase transformation and is well supported by HRTEM and magnetic measurements. The behavior of magnetic and electrical properties is well supported by the poly- and single-crystalline nature of YIG and Ce-YIG, respectively. The crystal structure transformation in YIG brought about by Ce substitution could unveil enormous opportunities in the preparation of single-crystal materials from their polycrystalline counterparts.

A New Approach of Preparing Nanocrystalline Bi-YIG Films

Research of preparing Bi substituted yttrium iron garnet and epoxy magneto-optical hybridized films

Comparison on the crystallization characteristics of sol–gel derived (BiDy)3Fe5O12 garnet film and powder

The Effect of pH value on the nano-particle size of bi substituted yttrium iron garnet

MAGNETO-OPTICAL PROPERTIES OF NANOMETER SCALE Bi:YIG FILMS

Preparation and Faraday Rotation of Bi-Yig/Pmma Nanocomposite

Influence of Surfactants on Co-Precipitation Synthesis of Bi–YIG Particles

Preparation of YAG Nanoparticles by Sol-Gel and Their Application in Electrical Contact Material

GELATION AND ANNEALING PROCESS OF PREPARING NANOCRYSTALLINE Y3Fe5O12 (YIG) BY SOL-GEL METHOD

Synthesis of Yig Nanopowders by Sol-Gel Method

Polycrystalline to preferred-(100) single crystal texture phase transformation of yttrium iron garnet nanoparticles

Preparation of YIG Single Crystal Nanofibers Via an Electrospinning Technique

Preparation and annealing process of Y3Fe5O12 by sol-gel method

Synthesis of Bi4-xYxTi3O12 Nanopowders by a Sol-Gel Process

Long Bi2s3 Nanowires Prepared by A Simple Hydrothermal Method

Polycrystalline Bi Substituted YIG Ferrite Processed Via Low Temperature Sintering

Supplemental Materials for “ Photo-Spin-Voltaic Effect ”

Synthesis of Bi4-xyxTi3O12 nanppowders by a sol-gel process

Preparation of (BiAl)DyIG garnet magneto-optical recording films by sol-gel method

The Magnetic and Magneto-optical Properties of Heavily Bi-Doped YIG (bi: YIG) Sputtering Film Annealed by RTA Method

Preparation and Magnetic Properties of Low Temperature Sintering Bi-Substituted Yttrium Iron Garnet