Abstract:Herein, bismuth–yttrium iron garnet (Bi-YIG) doped with In 3+ ions with chemical formula Y 2 BiIn x Fe 5−x O 12 ( x = 0.00–0.75 in steps of 0.15) was successfully prepared using solid-state reaction method. Effects of In 3+ -ion doping on microstructural, magnetic, and dielectric properties of Bi-YIG ferrite are investigated and discussed. Results show that In doping does not change the phase of Bi-YIG ferrite but increases lattice constant. Microstructure analysis indicates that In doping not only results in uniform grain shape but also influences grain size (the maximum average size is 3.46 μm at x = 0.30). Vibrating sample magnetometry results reveal that upon increasing In 3+ -ion content from x = 0.00 to x = 0.75, saturation magnetization first increases from 14.48 to 24.71 emu/g (at x = 0.45) and then decreases to 15.43 emu/g (at x = 0.75). Ferromagnetic resonance linewidth first decreases from 538.5 to 384.7 Oe (at x = 0.30) and then increases to 416.5 Oe (at x = 0.75). Real part of the permeability increases from 17.1 ( x = 0.00) to 21.2 ( x = 0.45) and then decreases to 19.5 ( x = 0.75) in frequency range from 1 MHz to 1 GHz. Additionally, In doping leads to the dielectric constant reaching a maximum value of ε' = 20.4 at x = 0.15, while maintaining low dielectric loss of ~ 10 −4 at the frequency of 10 GHz. Prepared material can be employed in high-frequency circulators, isolators, and microwave devices.

Effect of Bi-Substitution on the Dielectric Properties of Polycrystalline Yttrium Iron Garnet

Effects of Bi-Substitution on Dielectric and Ferroelectric Properties of Yttrium Iron Garnet Ceramics

Electrcal Investigation of Bi-substituted Yttrium Iron Garnet Using Complex Impedance Spectroscopy

Complex Impedance Spectroscopy of Bi-Substituted Yttrium Iron Garnet (YIG)

Preparation and Magnetic Properties of Low Temperature Sintering Bi-Substituted Yttrium Iron Garnet

High Dielectric Constant and Magnetic Properties of Bi-In Co-substituted YIG Ferrites

Magnetic and Magnetodielectric Properties of Bi-substituted Yttrium Iron Garnet Ceramics

Microstructure and Densification Mechanism of Low Temperature Sintering Bi-Substituted Yttrium Iron Garnet

Polycrystalline Bi Substituted YIG Ferrite Processed Via Low Temperature Sintering

Research of preparing Bi substituted yttrium iron garnet and epoxy magneto-optical hybridized films

The Effect of Bi Substitution on Phase Formation and Low Temperature Sintering of Y-Type Hexagonal Ferrite

Electrical, magnetic, and Raman spectroscopic studies on Bi-modified YIG ceramics

Enhanced Microwave Magnetic and Dielectric Properties of YBiIG Ferrite by Ca-Zr Co-substitution

Enhanced magnetic and dielectric properties of In3+-doped Y2BiInxFe5−xO12 ferrites for microwave device applications

DIELECTRIC PROPERTIES OF BISMUTH ZINC NIOBATE CERAMICS

Influence of Surfactants on Co-Precipitation Synthesis of Bi–YIG Particles

Kerr rotation spectra of Bi‐substituted polycrystalline YCaVIn iron garnets

The Multiferroic Properties Of Polycrystalline Bi1-Xyxfeo3 Films

Kerr Rotation Spectra Of Bi-Substituted Polycrystalline Ycavln Iron Garnets

The Effect of pH value on the nano-particle size of bi substituted yttrium iron garnet

Enhanced magnetic and dielectric properties of In 3+ -doped Y 2 BiIn x Fe 5−x O 12 ferrites for microwave device applications