Abstract:Liquid-phase epitaxy (LPE) is one of the best techniques for the preparation of single crystal garnet films. However, the specific Faraday rotation angle of Yttrium iron garnet (YIG) is small, and its easy magnetization axis is parallel to the film surface. The YIG requires a large external saturation field, which cannot meet the development needs of magneto-optical devices. It is found that Bi-substituted YIG(Bi:YIG) film has a larger specific Faraday angle. By adjusting the easy magnetization axis of Bi: YIG perpendicular to the film surface, the saturation magnetization of Bi: YIG can be reduced, so that it can work under a small external magnetic field. This meets the development needs of miniaturization and energy saving of magneto-optical device. The saturation magnetization of garnet film can be effectively reduced by substituting Ga3+ for YIG crystal, mainly for Fe3+ at the 24d position of its tetrahedron. And the lattice constants of Gd3Ga5O12 (GGG) and YIG are 1.2383 nm and 1.2376 nm, respectively. However, the radius of Bi3+ (10.8 nm) is larger than that of Y3+ (9.0 nm), the lattice mismatch of garnet film increases with the incorporation of Bi3+. In order to neutralize the lattice expansion caused by Bi3+, Tm3+ (8.69 nm) with a radius smaller than that of Y3+ (9.0 nm) is selected. Based on the theoretical analysis of the magnetocrystalline anisotropy of garnet film, (BiTm)3(GaFe)5O12 mono-crystalline films with different growth temperatures and different thickness values are grown by LPE on GGG (111) substrates. The experimental results show that when the thickness of epitaxial film is greater than 1 μm, the influence of shape anisotropy on magnetocrystalline anisotropy can be ignored. With the increase of growth temperature, the substitution number of Bi3+ ions decreases gradually, the lattice constant of epitaxial film decreases gradually, and the lattice mismatch first decreases and then increases. Then, the state of compressive stress gradually changes into that of tensile stress. Compared with growth-induced anisotropy, the stress-induced anisotropy is dominant in the change of magnetocrystalline anisotropy. The Verdet constant of (BiTm)3(GaFe)5O12 film is 11.8 × 104 rad/Tm@1064 nm. The results show that the prepared (BiTm)3(GaFe)5O12 mono-crystalline films have great development potential in magneto-optical devices.

Comparison on the crystallization characteristics of sol–gel derived (BiDy)3Fe5O12 garnet film and powder

Sputter deposition of bismuth and aluminum substituted dysprosium iron garnet films using sol-gel derived targets

Preparation of bismuth substituted dysprosium iron garnet film by a sol-gel process

A New Approach of Preparing Nanocrystalline Bi-YIG Films

Characterization of Bi-Substituted Dysprosium Iron Garnet Films Prepared by Sol-Gel Process

The Sol-Gel Preparation Procedure and Sintering Behavior of GdAlO_3

Research of preparing Bi substituted yttrium iron garnet and epoxy magneto-optical hybridized films

Preparation and annealing process of Y3Fe5O12 by sol-gel method

Preparation of (BiAl)DyIG garnet magneto-optical recording films by sol-gel method

Microstructure and Densification Mechanism of Low Temperature Sintering Bi-Substituted Yttrium Iron Garnet

Preparation and Characterization of Nanocrystalline (1−x)bisco3–xpbtio3 Powder

Structure and magneto-optical properties of fine-grain garnet thin film prepared by pyrolysis method

GELATION AND ANNEALING PROCESS OF PREPARING NANOCRYSTALLINE Y3Fe5O12 (YIG) BY SOL-GEL METHOD

Annealing Effects On Properties Of Bi-Substituted Garnet Films With Perpendicular Anisotropy Prepared By A Sol-Gel Method

Thermal behavior of gadolinium-silica gels prepared via sol–gel route combined to γ-irradiation process

Preparation and Orientation Mechanism Analysis of (bitm)3(gafe)5o12 Magneto-Optical Single Crystal Film with Out-of-plane Orientation

Polycrystalline to preferred-(100) single crystal texture phase transformation of yttrium iron garnet nanoparticles

Microwave/Millimeter-Wave Garnet Films

Effects of Synthetic Parameters in Pechini Method on the Formation and Properties of (zro2)0.92(sc2o3)0.08 Solid Solution

Gelation and heat treatment of preparing BaNd2Ti5O14 with autocombustion methods

Solid-state Grain Growth of Garnet Single Crystals of Complex Composition