STUDY ON FABRICATION AND SINTERING OF Al2O3 COMPOSITE POWDER COATED WITH NANO-SIZED BN

李永利,乔冠军,金志浩

DOI: https://doi.org/10.3321/j.issn:0454-5648.2002.04.017

2002-01-01

Abstract:α-Al2O3 powders coated with nanometer t (turbostratic)-BN were prepared through chemical processes using boric acid and urea as boron nitride source. The t-BN coatings were turned into the h-BN coatings in the nitrogen environment with a pressure of 0.52-0.53 MPa by heating the nanocomposite powders up to 1400-1600°C or by hot-pressing. The semi-finished compounds of Al-O-B reacted with N2, and BN was obtained. With 10% Si3N4 (in mass) as sintering aids, the Al2O3/30%BN (in volume) nanocomposite powders were hot-pressed at 1700°C which was 150°C lower than that without sintering aids, and the densification materials with almost no pore were obtained. The hot-pressed body has a high fracture strength of 446 MPa and can be drilled easily using a hard alloy drill tip.