Design and Fabrication of Machinable Al₂O₃/h-BN Composites and FGMs

Zhen Zhu Cao,Wei Pan,Ming Hao Fang,Rui Gang Wang

DOI: https://doi.org/10.4028/www.scientific.net/MSF.423-425.203

2003-01-01

Materials Science Forum

Abstract:Machinable Al2O3/h-BN composites and seven-layered functionally graded materials (FGM) with h-BN addition ranged from 0 similar to 30vol% were successfully fabricated by spark plasma sintering (SPS). SEM analysis revealed that the h-BN mainly distributed at the grain boundaries of Al2O3 grains, and Vickers's hardness of the composites decreased with the addition of h-BN. Preferred orientation of h-BN grain was observed by XRD results and confirmed by arranged BN grains perpendicular to pressure direction in SEM images. The relative density of the 30vol% h-BN/Al2O3 composite reached up to 97% whose Vickers's hardness was as high as 4.7GPa, which can be drilled easily using carbide cenmented drill. The seven-layered functionally graded material was prepared by powder layering and spark plasma sintering. Its interface between layers observed with optical microscopy became unclear. Element line-scan analysis demonstrated that the boron element distributed gradually in stepwise way.