Abstract:In this study, three types of three-layer functionally graded materials (FGMs) were designed by mainting the average content of the reinforcement constant and changing the span of the composition. The B 4 C particle-reinforced Al-matrix FGMs and a homogeneous composite (HC) with the same average composition were prepared using the laser additive manufacturing technique. The FGMs had a higher average secondary-phase content and grain size than the HC. Large (black) and reticulated (white) secondary phases corresponding to B 4 C phase, T phase, and MgZn 2 were observed in the as-deposited FGM samples. The content of the secondary phase in the middle layer was generally low. The bottom layer, which was in direct contact with the substrate, exhibited the smallest grain size. The hardness and wear resistance significantly improved owing to the high B 4 C content in the top layer. The flexural behaviors of each layer of the FGM in different directions were systematically studied. The plasticity of the single-layer material decreased with increase in the B 4 C content. When the bottom layer had a high B 4 C content, the flexural ability significantly reduced. Among all the samples, G2 with 8% B 4 C particle content in the top layer exhibited the best comprehensive mechanical properties. The hardness value, wear rate of the top layer, maximum bending stress, and maximum bending strain of the FGM were 177.5 HV, 0.367 × 10 −3 mm 3 /(N·m), 585.6 MPa, and 7.36%, respectively. This study can provide a reference value for the future design and development of wear-resistant gradient materials for aerospace applications.

TiB<sub>2</sub>/AlN/Cu Functionally Graded Materials (FGMs) Fabricated by Spark Plasma Sintering (SPS) Method

TiB<sub>2</sub>/AlN/Cu Functionally Graded Materials (fgms) Fabricated by Spark Plasma Sintering (SPS) Method

TiB2/Cu Electrode Material Fabricated Via SPS

Spark Plasma Sintering of Functionally Graded Material in the Ti–TiB2–B System

Preparation of Functionally Graded Cu/AlN/Cu Electrode Materials for Thermoelectric Devices

A Novel Functionally Graded Material in the Ti–Si–C System

Functionally Graded Electrode Materials for Thermoelectric Devices

Cu/AlN composite and functionally graded materials with high strength and high electrical- and thermal-conductivity fabricated by spark plasma sintering

Synthesis of Functionally Graded AA7075-B4C Composite with Multi-Level Gradient Structure

Fabrication of Al2O3/TiC/Ni Functionally Graded Materials by Pulsed-Electric Current Sintering and Their Mechanical Properties.

A novel functionally graded material in the ZrB2–SiC and ZrO2 system by spark plasma sintering

Fabrication Of Sic/Cu Functionally Gradient Material By Graded Sintering

Preparation of Cu/SiC FGM by Coating Method and SPS Sintering

The Fabrication of Ticn-Based Functionally Graded Cermets by Spark Plasma Sintering

Preparation and characterization of Al2O3–Ti3SiC2 composites and its functionally graded materials

Microstructure and Mechanical Properties of Ti60-Ti2alnb Functionally Graded Materials Fabricated by Laser Directed Energy Deposition

Spark Plasma Sintering of AlN/Al Functionally Graded Materials

Effects of TiB2 content and gradient structure on microstructural characterization and mechanical properties of TiB2/Al7050 composites

Composition design and mechanical properties of B 4 C/Al-Zn-Mg-Cu functionally graded materials prepared by laser additive manufacturing

Combustion synthesis TiC-Al2O3/Fe FGM and its resisting thermal shock behaviors

In Situ Multi-Layer Functionally Graded Materials by Electromagnetic Separation Method